Magnesium phosphate glasses co-doped with Er3+/Nd3+ concentration were prepared using melt quenching technique and thermal annealing process was proposed to control any defects found in the glass samples. The physical and optical properties of the samples were investigated. The amorphous nature of the samples were confirmed using X-ray diffraction pattern. It shows that all samples are in amorphous state. The optical band gaps and Urbach energies were obtained from the optical absorption spectra. The studyshows that the optical band gap energy,Eopt isincreasingas the Nd2O3 content increased. Meanwhile, Urbach energies, ΔE decreased due to increase of Nd2O3 content. The results obtained from this study shows that the optical band gap, Eopt and the Urbach energy, ΔE are intherange of 3.95 –3.98 eV and 0.367 –0.437 eV respectively.
Glasses with chemical composition of (60-x)P2O5-25ZnO-(15+x)Li2O with 0.0 ≤ x ≤ 5.0 mol % are prepared by melt quenching technique. The physical properties, by mean of density and molar volume are determined. The amorphous nature, absorption and structural behaviour are characterized using X-ray Diffraction (XRD), Ultraviolet-visible-near infrared (UV-Vis-NIR) and Fourier transform infrared (FTIR) respectively. In this work, the glass densities are found increases in the range of 2.70 - 2.78 gcm-3 and molar volume decreases from 37.48 - 40.75 gcm-3 with respect to Li2O concentration. Meanwhile, the optical band gap energy for direct and indirect transition are found decreases from 3.074 eV to 2.525 eV and 2.699 eV to 1.670 eV respectively. The Urbach energy is varies as Li2O content increases. The refractive index of these glasses is ranging from 2.48 to 2.90. FTIR spectra exhibited seven bands which centered at 512 cm−1, 767 cm−1, 918 cm−1, 1087 cm−1, 1281 cm−1, 1627 cm−1 and 3441 cm−1 wavenumber that assigned as vibration of Zn-O, symmetric stretching vibration of P-O-P rings, asymmetric stretching vibration of P-O-P groups, asymmetric stretching of PO2-group, asymmetric stretching vibration P=O, bending vibration of water molecule and fundamental stretching of hydroxyl group.
Achieving tuneable photoluminescence via controlled co-doping of rare earth ions in lithium niobate based glasses are challenging. A series of Er3+/ Nd3+ co-doped tellurite glasses of composition (70-x-y) TeO2 – 15 Li2CO3 – 15 Nb2O5 – (x) Er2O3 – (y) Nd2O3 with x = 0; 1.0 mol % and 0 ≤ y ≤ 1.0 mol % are prepared using melt quenching technique. The influence of co-dopants on the emission properties is analyzed and discussed using partial energy level diagram of rare earth ions. The dopants concentration dependent physical properties such as refractive index, molar volume, density, polarizability and molar refractions are determined. The down-converted luminescence spectra for 2G9/2 à4I9/2 transition reveal a strong green emission band centred at 497 nm is attributed to the energy transfer from erbium to neodymium ion. The emission spectra exhibit five prominent peaks centred at 497, 539, 553, 616 and 634 nm corresponding to the transitions from 2H11/2, 4S3/2 and 4F9/2 excited states to the ground state of Er3+ ion and the transitions from 2G9/2, 2G7/2, 2H11/2 and 4F9/2 excited states to ground state of Nd3+ ion. The highest intensity is achieved for x = y = 1.0 mol%. The excellent luminescence response suggests that our glasses may be nominated for solid state lasers and other photonic applications.
The phosphate glasses, with composition (60-x)P2O5-25ZnO-(15+x)Li2O where 0.0 ≤ x ≤ 5.0 mol% are prepared by conventional melt quenching method. The amorphous nature of the glass is determined by X-Ray Diffraction (XRD). The physical properties are measured in term of their density and molar volume. Glass density is found to increase from 2.700 to 2.785 g cm-3 whereas molar volume is found to decrease from 40.735 to 37.488 cm3 mol-1 with respect to Li2O content. The DC measurements are done by using four point probes and the activation energies are determined. Arrhenius plot shows straight line behavior as observed that confirmed the conductivity increased with Li2O content. The activation energy is found to decreases from 0.75 to 0.08 eV as Li2O content is increased in the temperature range from 310 to 420 K. Measurements of the thermal conductivity using Lee’s disc apparatus have been made. It is observed that the maximum and minimum thermal conductivity are 0.2679 and 0.2168 W m-1 K-1 respectively.
Understanding the mechanism of visible luminescence enhancement from rare earth doped glasses containing metallic nanoparticles (NPs) is the challenging issue. The photoluminescence (PL) spectra of Er3+: Au-doped tellurite glass is investigated for different concentration of gold NPs. A series of glasses with composition (70-x) TeO2-30 ZnO-0.5 Er2O3x Au where x = (0.1, 0.3, 0.5 mol%) are prepared by melt-quenching method. The thermal parameters such as the glass transition (Tg), crystallization temperature (Tc) and melting temperature (Tm) are determined using DTA thermogram. PL spectra exhibit two distinct peaks at 493nm and 550nm which are assigned to the2H11/2-4I15/2and4S3/2-4I15/2transition respectively. The influence of gold NPs in enhancing the luminescence intensity under the 360nm excitation wavelength is observed understood.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.