The present study reports on the kinetics of borided Nickel 201 alloy. The thermochemical treatment of boronizing was carried out in a solid medium consisting of B 4 C and KBF 4 powders mixture at 1123, 1173 and 1223 K for 2, 4 and 6 h, respectively. The boride layer was characterized by optical microscopy, X-ray diffraction technique and micro-Vickers hardness tester. X-ray diffraction analysis revealed the existence of NiB, Ni 2 B, Ni 3 B and Ni 4 B 3 compounds at the surface of borided Nickel 201 alloy. The thickness of the boride layer increased with an increase in the boriding time and the temperature. The hardness of the nickel borides formed on the surface of the nickel substrate ranged from 1642 to 1854 HV 0.05 , whereas the Vickers hardness value of the untreated nickel was 185 HV 0.05. The growth kinetics of boride layers forming on the borided Nickel 201 alloy was also analysed. The boron activation energy (Q) was estimated as equal to 203.87 kJ mol −1 for the borided Nickel 201 alloy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.