Using the layer-by-layer (LbL) assembly technique to deposit mechanically reinforcing coatings onto porous templates is a route for fabricating engineered bone scaffold materials with a combination of high porosity, strength, and stiffness. LbL assembly involves the sequential deposition of nano-to micro-scale multilayer coatings from aqueous solutions. Here, a design of experiments (DOE) approach was used to evaluate LbL assembly of polyethyleneimine (PEI), polyacrylic acid (PAA), and nanoclay coatings onto open-cell polyurethane foam templates. The thickness of the coatings, and the porosity, elastic modulus and collapse stress of coated foam templates were most strongly affected by the pH of PAA solutions, salt concentration, and interactions between these factors. The mechanical properties of coated foams correlated with the thickness of the coatings, but were also ascribed to changes in the coating properties due to the different assembly conditions. A DOE optimization aimed to balance the trade-off between higher mechanical properties but lower porosity of foam templates with increasing coating thickness. Micromechanical modelling predicted that deposition of 116 QLs would achieve mechanical properties of cancellous bone (>0.05 GPa stiffness and >2 MPa strength) at a suitable porosity of >70%. When capped with a final layer of PAA and cross-linked via thermal treatment, the PEI/PAA/PEI/nanoclay coatings exhibited good indirect cytotoxicity with mesenchymal stem cells. The ability of LbL assembly to deposit a wide range of functional constituents within multilayer-structured coatings makes the general strategy of templated LbL assembly a powerful route for fabricating engineered tissue scaffolds that can be applied onto various porous template materials to achieve a wide range of properties, pore structures, and multifunctionality.
In this study, thermoresponsive copolymers that are fully injectable, biocompatible, and biodegradable and are synthesized via graft copolymerization of poly(N-isopropylacrylamide) onto alginate using a free-radical reaction are presented. This new synthesis method does not involve multisteps or associated toxicity issues, and has the potential to reduce scale-up difficulties. Chemical and physical analyses verify the resultant graft copolymer structure. The lower critical solution temperature, which is a characteristic of sol-gel transition, is observed at 32 °C. The degradation properties indicate suitable degradation kinetics for drug delivery and bone tissue engineering applications. The synthesized P(Alg-g-NIPAAm) hydrogel is noncytotoxic with both human osteosarcoma (MG63) cells and porcine bone marrow derived mesenchymal stem cells (pBMSCs). pBMSCs encapsulated in the P(Alg-g-NIPAAm) hydrogel remain viable, show uniform distribution within the injected hydrogel, and undergo osteogenic and chondrogenic differentiation under appropriate culture conditions. Furthermore, for the first time, this work will explore the influence of alginate viscosity on the viscoelastic properties of the resulting copolymer hydrogels, which influences the rate of medical device formation and subsequent drug release. Together the results of this study indicate that the newly synthesized P(Alg-g-NIPAAm) hydrogel has potential to serve as a versatile and improved injectable platform for drug delivery and bone tissue engineering applications.
A range of bone regeneration strategies, from growth factor delivery and/or mesenchymal stem cell (MSC) transplantation to endochondral tissue engineering, have been developed in recent years. Despite their tremendous promise, the clinical translation and future use of many of these strategies is being hampered by concerns such as off target effects associated with growth factor delivery. Therefore the overall objective of this study was to investigate the influence of alpha-tricalcium phosphate (α-TCP) nanoparticle delivery into MSCs using a RALA cell penetrating peptide on osteogenesis in vitro and both intramembranous and endochondral bone formation in vivo. RALA conjugated α-TCP nanoparticle delivery to MSCs resulted in an increased expression of bone morphogenetic protein-2 (BMP-2) and an upregulation in a number of key osteogenic genes. When α-TCP stimulated MSCs were encapsulated into alginate hydrogels, enhanced mineralization of the engineered construct was observed over a 28 day culture period. Furthermore, the in vivo bone forming potential of RALA conjugated α-TCP nanoparticle delivery to MSCs was found to be comparable to growth factor delivery. Recognizing the potential and limitations associated with endochondral bone tissue engineering strategies, we then sought to explore how α-TCP nanoparticle delivery to MSCs influences early mineralization of engineered cartilage templates in vitro and their subsequent ossification in vivo. Despite accelerating mineralization of engineered cartilage templates in vitro, RALA conjugated α-TCP nanoparticle delivery did not enhance endochondral bone formation in vivo. Therefore the potential of RALA conjugated α-TCP nanoparticle delivery appears to be as an alternative to growth factor delivery as a single stage strategy for promoting bone generation.3
Calcium phosphate-base materials (e.g., alpha tri-calcium phosphate (α–TCP)) have been shown to promote osteogenic differentiation of stem/progenitor cells, enhance osteoblast osteogenic activity and mediate in vivo bone tissue formation. However, variable particle size and hydrophilicity of the calcium phosphate result in an extremely low bioavailability. Therefore, an effective delivery system is required that can encapsulate the calcium phosphate, improve cellular entry and, consequently, elicit a potent osteogenic response in osteoblasts. In this study, collagenous matrix deposition and extracellular matrix mineralization of osteoblast lineage cells were assessed to investigate osteogenesis following intracellular delivery of α-TCP nanoparticles. The nanoparticles were formed via condensation with a novel, cationic 30 mer amphipathic peptide (RALA). Nanoparticles prepared at a mass ratio of 5:1 demonstrated an average particle size of 43 nm with a zeta potential of +26 mV. The average particle size and zeta potential remained stable for up to 28 days at room temperature and across a range of temperatures (4–37 °C). Cell viability decreased 24 h post-transfection following RALA/α-TCP nanoparticle treatment; however, recovery ensued by Day 7. Immunocytochemistry staining for Type I collagen up to Day 21 post-transfection with RALA/α-TCP nanoparticles (NPs) in MG-63 cells exhibited a significant enhancement in collagen expression and deposition compared to an untreated control. Furthermore, in porcine mesenchymal stem cells (pMSCs), there was enhanced mineralization compared to α–TCP alone. Taken together these data demonstrate that internalization of RALA/α-TCP NPs elicits a potent osteogenic response in both MG-63 and pMSCs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.