Photoluminescence (PL) from hydrogenated silicon carbide (SiC:H) films is studied at room temperature. The films were deposited by plasma-enhanced chemical vapor (PECVD) technique with and without substrate bias using methyltrichlorosilane as a main precursor. After the deposition the samples were annealed at various temperatures in vacuum. The films were characterized by atomic force microscopy (AFM), Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD). The samples deposited without substrate bias (series A) were amorphous, whereas the samples deposited with negative substrate bias -100V (series B) were nanocrystalline. The one-peak (470 nm) and double-peak (415 and 437 nm) PL structures of the as-deposited samples A and B were observed, respectively. Annealing strongly enhanced intensity of PL of the samples B and trandformed PL spectrum from double-peak into broad featureless band with intensity at about 470 nm. The blue PL in as-deposited films B is supposed to be assigned to the radiative recombination in the sites located at the nanocrystallite surface, whereas the photo excitation of carries mostly occurs in nanocrystallite cores. A further increase in annealing temperature causes hydrogen effusion, which leads to an increase of the concentration of non-raidative recombination centers associated with dangling-bonds and as a result, to the quenching of PL.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.