In the present work, attempts of reducing a graphene oxide powder using a low temperature hydrogenation disproportionation desorption and the recombination process (L-HDDR) has been carried out. A lower processing temperature in large scale production is significant when costs are concerned. Graphite oxide was prepared using a modified Hummers’ method dispersed in ethanol and exfoliated using ultrasonication to produce Graphene Oxide (GO). Investigations have been carried out by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The experimental results of L-HDDR processing graphene oxide powder, using unmixed hydrogen at 400°C and relatively low pressures (<2 bars) have been reported. X-ray diffraction patterns showed a reduction of graphene oxide with the L-HDDR process. The results showed that both processes, the L-HDDR as well as the standard HDDR, may be applied to the reduction of graphene oxide in order to produce supercapacitor materials. The advantage of employing the L-HDDR process is a relatively low temperature reducing the cost of treatment, what is a very important factor for producing a large amount of material. Thus, the L-HDDR process has been considered a promising alternative method of reducing graphene oxide with efficiency, with the possibility of large scale production.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.