Poly(lactic acid) (PLA) was melt mixed in a laboratory extruder with poly(butylene adipate-co-terephthalate) (PBAT) and poly(butylene succinate) (PBS) in the presence of polypropylene glycol di glycidyl ether (EJ400) that acted as both plasticizer and compatibilizer. The process was then scaled up in a semi-industrial extruder preparing pellets having different content of a nucleating agent (LAK). All of the formulations could be processed by blowing extrusion and the obtained films showed mechanical properties dependent on the LAK content. In particular the tearing strength showed a maximum like trend in the investigated composition range. The films prepared with both kinds of blends showed a tensile strength in the range 12–24 MPa, an elongation at break in the range 150–260% and a significant crystallinity.
In this work, composites based on poly(3-hydroxybutyrate-3-hydroxyvalerate) (PHB-HV) and waste wood sawdust (SD) fibers, a byproduct of the wood industry, were produced by melt extrusion and characterized in terms of processability, thermal stability, morphology, and mechanical properties in order to discriminate the formulations suitable for injection molding. Given their application in agriculture and/or plant nursery, the biodegradability of the optimized composites was investigated under controlled composting conditions in accordance with standard methods (ASTM D5338-98 and ISO 20200-2004). The optimized PHB-HV/SD composites were used for the production of pots by injection molding and their performance was qualitatively monitored in a plant nursery and underground for 14 months. This study presents a sustainable option of valuation of wood factory residues and lowering the production cost of PHB-HV-based compounds without affecting their mechanical properties, improving their impact resistance and biodegradability rates in terrestrial environments.
Bio-composites based on polyhydroxyalkanoates (PHAs) and fibres of Posidonia oceanica (PO) were investigated to assess their processability by extrusion, mechanical properties, and potential biodegradability in a natural marine environment. PHAs were successfully compounded with PO fibres up to 20 wt % while, at 30 wt % of fibres, the addition of 10 wt % of polyethylene glycol (PEG 400) was necessary to improve their processability. Thermal, rheological, mechanical, and morphological characterizations of the developed composites were conducted and the degradation of composite films in a natural marine habitat was evaluated in a mesocosm by weight loss measure during an incubation period of six months. The addition of PO fibres led to an increase in stiffness of the composites with tensile modulus values about 80% higher for composites with 30 wt % fibre (2.3 GPa) compared to unfilled material (1.24 GPa). Furthermore, the impact energy markedly increased with the addition of the PO fibres, from 1.63 (unfilled material) to 3.8 kJ/m2 for the composites with 30 wt % PO. The rate of degradation was markedly influenced by seawater temperature and significantly promoted by the presence of PO fibres leading to the total degradation of the film with 30 wt % PO in less than six months. The obtained results showed that the developed composites can be suitable to manufacture items usable in marine environments, for example, in natural engineering interventions, and represent an interesting valorisation of the PO fibrous wastes accumulated in large amounts on coastal beaches.
Poly(lactic acid)/triacetine plasticized cellulose acetate (PLA/pCA) blends were prepared by extrusion at two different temperatures and tetrabutylammonium tetraphenyl borate (TBATPB) was added as a transesterification catalyst to reactively promote the formation of PLA-CA copolymer during the reactive extrusion. The occurrence of chain scission in the PLA phase and branching/crosslinking in the CA phase in the presence of TBATPB, resulting also in a darkening of the material, were demonstrated by studying torque measurements and by performing proper thermogravimetric tests on CA with the different additives. Tensile and impact tests onto the blends prepared at the lower temperature showed better properties than the ones obtained at a higher temperature. Then, the mechanical properties of PLA/plasticized cellulose acetate (pCA) blends prepared at the lower temperature were investigated as a function of the content of plasticized CA in the blend. A range of compositions was observed where blends exhibited improved impact properties with respect to pure PLA without a significant decrease in their elastic modulus. The study of the phase morphology of the blends revealed that the occurrence of reactive compatibilization did not significantly affect the phase distribution. In general, fibrillar CA particles were formed in the PLA matrix during extrusion, thus allowing the preparation of CA fibre reinforced composites. The trend of morphology as a function of the composition and processing conditions was then discussed by considering the evolution of phase morphology in immiscible polymer blends.
In order to produce sustainable, bio-based and highly biodegradable materials, composites based on poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV) and fibers of Posidonia oceanica (PO), a dominant Mediterranean seagrass, were produced by simple melt mixing and characterized in terms of thermal stability, morphology and rheological/mechanical properties. In view of their potential application in marine environments, degradation of the developed composites was evaluated under simulated and real marine environmental conditions for 1 year. Using 10 wt % of acetyl tributyl citrate (ATBC) as a plasticizer, smooth processing was achieved for up to 30 wt % of PO fibers, despite the reduction of the melt fluidity observed with increasing fiber loading. The tensile modulus slightly increased (from 2 to 2.4 GPa) while the tensile strength and the elongation decreased (from 23.6 to 21.5 MPa and from 3.2 to 1.9%, respectively) by increasing the PO fiber content from 0 to 30 wt %. Interestingly, the impact resistance of the composites increased with the increasing of the PO content: the Charpy’s impact energy increased from 3.6 (without fiber) to 4.4 kJ/m2 for the composite with 30 wt %. The results of the aerobic biodegradation under simulated marine conditions showed that the presence of PO fibers favored the physical disintegration of the composite increasing the biodegradation rate of the polymeric matrix: after 216 days, the composite with 20 wt % PO fibers showed a biodegradability of about 30% compared to 20% of the composite without fibers. Under real marine conditions, the specimens containing PO fibers showed higher weight losses and deterioration of tensile properties compared to those without fibers. Presumably, biodegradation occurred after colonization of the specimen, and the specimens with 20 wt % PO fibers showed well-developed biofilm consisting of bacteria and fungi on the surface after only 3 months of incubation in marine sediments, unlike the no-fiber specimens. Consequently, the persistence of an adequate mechanical performance for a relatively long period (1 year), due to a moderate rate of biodegradation in the marine environment, make the developed PHBV/PO composites particularly suitable for the production of relatively low-cost and biodegradable items which are usable in the sea and/or sand dunes, increasing the market opportunities for biopolymers such as PHBV and, at the same time, finding an eco-sustainable valorization for the PO fibrous residues accumulated in large quantities on Mediterranean beaches, which represents a problem for coastal municipalities.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.