The asphalt pavement susceptibility was influenced by traffic load and temperature. Therefore, modified asphalt has been done to improve the asphalt performance. Depolymerized block skim rubber (BSR) was used as asphalt modifier. BSR is a low quality crumb rubber, which made from skim (byproduct of creamed latex). This investigation aims to determine effect of depolymerization of BSR on the physical performance of modified asphalt. Initially, BSR was depolymerized by mechanical action (mastication) with different time of 8, 16, and 24 min. Then, the asphalt modifier, depolymerized BSR was added to asphalt with different ratio 3, 5, 7%. The softening point and mixing time of asphalt were compared with modified asphalt. The performance of modified asphalt showed that asphalt modifiers increased the softening point and mixing time of asphalt. Maximum softening point reached 54.30C by 7% BSR (16 min. of mastication time). The modified asphalt had 25.70C softening point higher than asphalt. It was conclude that depolymerized BSR can increase the performance of asphalt (softening point), although increase the mixing time of it. Moreover, it could give alternative to reduce cost of modified asphalt pavement making.
The improvement of the compatibility of natural rubber (NR)/acrilonitrile-butadiene rubber (NBR) blend on rubber seal vulcanizate has been done by the addition of chloroprene rubber (CR) or epoxidized natural rubber (ENR) as compatibilizer. Rubber seal compound was made of NR and NBR blend (BN) with CR (BCR), and ENR with epoxy content of 10% (BENR10), 20% (BENR20), 30% (BENR30), 40% (BENR40), and 50% (BENR50
ABSTRAKPeningkatan kompatibilitas pencampuran karet alam (KA) dan akrilonitril-butadiena (NBR) pada vulkanisat karet perapat dilakukan dengan menambahkan kompatibiliser karet kloroprena (CR) atau karet alam epoksidasi (KAE). Kompon karet perapat dibuat dari campuran KA dan NBR (BN) dengan kompatibiliser CR (BCR) dan KAE dengan kandungan epoksi 10% (BKAE10), 20% (BKAE20), 30% (BKAE30), 40% (BKAE40), dan 50% (BKAE50). Komposisi pada masing-masing formula diseragamkan dengan perbandingan KA:NBR sebesar 40:60 dan KA:kompatibiliser:NBR sebesar 40:5:55. Kompon divulkanisasi dengan sistem efisien pada suhu 150 0 C. Penambahan kompatibiliser CR memperbaiki karakteristik pematangan, pampatan tetap, dan ketahanan n-pentana vulkanisat KA/NBR (BN). Sedangkan penambahan kompatibiliser KAE memperbaiki sifat elastis vulkanisat. Keelastisan dan ketahanan n-pentana BKAE meningkat seiiring kandungan epoksi KAE.Kata kunci: karet perapat, kompatibiliser, ketahanan n-pentana, sifat mekanis.
PENDAHULUANKaret perapat (rubber seal) pada tabung gas liquified petroleum gas (LPG) dipasang untuk mencegah terjadinya kebocoran gas pada waktu pengisian atau penggunaan tabung LPG serta memperkuat kedudukan regulator. Pada pembuatan produk karet perapat, bahan baku karet yang digunakan harus tahan terhadap gas LPG. Pada SNI karet perapat (SNI 7655:2010), ketahanan karet terhadap gas LPG didekati melalui pengujian ketahanan karet terhadap pelarut non polar n-pentana. Salah satu alternatif bahan baku pembuatan karet perapat adalah karet akrilonitril butadiena (NBR). NBR memiliki ketahanan yang baik terhadap oli
Penggunaan material komposit karet alam sebagai alternatif material pembangun canal blocking merupakan hal yang baru. Tujuan penelitian adalah mengungkap sifat fisik dan ketahanan terhadap lingkungan asam lahan gambut komposit karet alam. Komposit karet alam didisain dengan nilai kekerasan yang bervariasi sebesar 70, 80 dan 90 Shore A dan jenis partikulat berupa karbon hitam dan kalsium karbonat (CaCO3). Data yang dikumpulkan menunjukkan bahwa formulasi komposit karet alam terbaik menggunakan partikulat CaCO3 sebanyak 140 bsk dan karbon hitam 65 bsk (berat satuan karet). Komposit karet ini memiliki sifat fisika dan ketahanan yang baik pada lingkungan asam lahan gambut ber-pH 3 (setara dengan larutan asam sulfat 20%) dan pH 2,5 (setara dengan larutan asam sulfat 40%), yang ditandai dengan kecilnya perubahan volume dan sifat fisika vulkanisat setelah perendaman dalam larutan asam sulfat 20% dan 40%.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.