Crystalline solids with extended non-interpenetrating three-dimensional crystal structures were synthesized that support well-defined pores with internal diameters of up to 48 angstroms. The Zn4O(CO2)6 unit was joined with either one or two kinds of organic link, 4,4',4''-[benzene-1,3,5-triyl-tris(ethyne-2,1-diyl)]tribenzoate (BTE), 4,4',44''-[benzene-1,3,5-triyl-tris(benzene-4,1-diyl)]tribenzoate (BBC), 4,4',44''-benzene-1,3,5-triyl-tribenzoate (BTB)/2,6-naphthalenedicarboxylate (NDC), and BTE/biphenyl-4,4'-dicarboxylate (BPDC), to give four metal-organic frameworks (MOFs), MOF-180, -200, -205, and -210, respectively. Members of this series of MOFs show exceptional porosities and gas (hydrogen, methane, and carbon dioxide) uptake capacities. For example, MOF-210 has Brunauer-Emmett-Teller and Langmuir surface areas of 6240 and 10,400 square meters per gram, respectively, and a total carbon dioxide storage capacity of 2870 milligrams per gram. The volume-specific internal surface area of MOF-210 (2060 square meters per cubic centimeter) is equivalent to the outer surface of nanoparticles (3-nanometer cubes) and near the ultimate adsorption limit for solid materials.

The concept and occurrence of isoreticular (same topology) series of metal-organic frameworks (MOFs) is reviewed. We describe the preparation, characterization, and crystal structures of three new MOFs that are isoreticular expansions of known materials with the tbo (Cu(3)(4,4',4''-(benzene-1,3,5-triyl-tris(benzene-4,1-diyl))tribenzoate)(2), MOF-399) and pto topologies (Cu(3)(4,4',4''-(benzene-1,3,5-triyl-tribenzoate)(2), MOF-143; Cu(3)(4,4',4''-(triazine-2,4,6-triyl-tris(benzene-4,1-diyl))tribenzoate)(2), MOF-388). One of these materials (MOF-399) has a unit cell volume 17 times larger than that of the first reported material isoreticular to it, and has the highest porosity (94%) and lowest density (0.126 g cm(-3)) of any MOFs reported to date.

Metal-organic framework-177 (MOF-177) is one of the most porous materials whose structure is composed of octahedral Zn4O(-COO)6 and triangular 1,3,5-benzenetribenzoate (BTB) units to make a three-dimensional extended network based on the qom topology. This topology violates a long-standing thesis where highly symmetric building units are expected to yield highly symmetric networks. In the case of octahedron and triangle combinations, MOFs based on pyrite (pyr) and rutile (rtl) nets were expected instead of qom. In this study, we have made 24 MOF-177 structures with different functional groups on the triangular BTB linker, having one or more functionalities. We find that the position of the functional groups on the BTB unit allows the selection for a specific net (qom, pyr, and rtl), and that mixing of functionalities (-H, -NH2, and -C4H4) is an important strategy for the incorporation of a specific functionality (-NO2) into MOF-177 where otherwise incorporation of such functionality would be difficult. Such mixing of functionalities to make multivariate MOF-177 structures leads to enhancement of hydrogen uptake by 25%.

Separation of acetylene from carbon dioxide and ethylene is challenging in view of their similar sizes and physical properties. Metal-organic frameworks (MOFs) in general are strong candidates for these separations owing to the presence of functional pore surfaces that can selectively capture a specific target molecule. Here, we report a novel 3D microporous cationic framework named JCM-1. This structure possesses imidazolium functional groups on the pore surfaces and pyrazolate as a metal binding group, which is well known to form strong metal-to-ligand bonds. The selective sorption of acetylene over carbon dioxide and ethylene in JCM-1 was successfully demonstrated by equilibrium gas adsorption analysis as well as dynamic breakthrough measurement. Furthermore, its excellent hydrolytic stability makes the separation processes highly recyclable without a substantial loss in acetylene uptake capacity.

MIL-101 and MIL-101-NH 2 were partially modified to incorporate various functional groups that are capable of forming hydrogen bonds with water. Specifically, MIL-101-NH 2 was partially functionalized with -NHCONHCH 2 CH 3 (-UR2), -NHCOCHCHCOOH (-Mal), or -NH(CH 2 ) 3 SO 3 H (-3SO 3 H) and MIL-101 was partially functionalized with -COOH in order to investigate the effect of these groups on the water sorption properties when compared to the pristine versions. The MIL-101 derivatives were synthesized by either post-synthetic modification of MIL-101-NH 2 or through direct synthesis using a mixed linker strategy. The ratios of the incorporated functional groups were determined by 1 H-NMR analyses and the porosity changes were revealed by N 2 gas adsorption measurements at 77 K. Water sorption isotherms at 298 K conclude that the incorporation of -3SO 3 H enhances the water vapour uptake capacity at a low relative pressure (P/P 0 ¼ 0.30), whereas -UR2 and -Mal retard water adsorption in MIL-101-NH 2 . The partial incorporation of -COOH in MIL-101 exhibits a steeper water uptake at lower pressure (P/P 0 ¼ 0.40) than MIL-101-NH 2 . Interestingly, a greater -COOH content within the MIL-101 framework reduces the water uptake capacity. These results indicate that even partial functionalization of MIL-101 induces noticeably large changes in the water adsorption properties.