Novel photochromic 1-vinylidene-naphtho[2,1-b]furan derivatives (VNF-1 and VNF-2) were successfully anchored onto silica nanoparticles (SiO NPs) through direct adsorption (SiO@VNF-1) and covalent post-grafting (SiO@VNF-2). SiO NPs with different sizes (15 ± 3 and 123 ± 7 nm) and surface chemistry (pH in the range of 5-9) were used, offering a wide range of possibilities to fabricate tailor-made photochromic materials. The characterization of VNF-based SiO NPs confirmed the efficient VNF immobilization and the integrity of both organic and inorganic components. The photochromic behavior of these new nanoparticles indicates that silica surface acidity and the type of VNF immobilization strategy (adsorption vs. covalent grafting) were crucial factors for the occurrence of photochromism in the VNF-based SiO NPs. Upon UV (λ = 365 nm) or sunlight exposure for 1 min, only the SiO@VNF-1 nanomaterials prepared by direct VNF adsorption onto SiO NPs with pH ≈ 6.0 showed direct and reversible photochromic properties, developing fast (in seconds) and intense salmon and violet coloration, with high values of total color difference () and optical densities (ΔOD = 0.14-0.25). In contrast, all nanomaterials prepared by covalent grafting of VNF-2 onto SiO NPs (SiO@VNF-2) did not exhibit photochromism. In the case of the photochromic SiO@VNF-1 NPs, the decoloration process followed a bi-exponential decay with fast rate constants (k = 1.6 × 10-1.6 min and k = 9.1 × 10-1.3 × 10 min), which were responsible for the loss of coloration in less than 10 min. Furthermore, they presented very good resistance to fatigue, showing reversibility between the colored/uncolored states without significant loss of their performance for at least 8 successive UV/dark cycles.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.