This study investigates a wide range of clinically relevant mechanical properties of poly(methyl methacrylate) (PMMA) denture base materials modified with di-methyl itaconate (DMI) and di-n-butyl itaconate (DBI) in order to compare them to a commercial PMMA denture base material. The commercial denture base formulation was modified with DMI and DBI by replacing up to 10 wt% of methyl methacrylate (MMA) monomer. The specimens were prepared by standard bath curing process. The influence of the itaconate content on hardness, impact strength, tensile, and thermal and dynamic mechanical properties was investigated. It is found that the addition of di-n-alkyl itaconates gives homogenous blends that show decreased glass transition temperature, as well as decrease in storage modulus, ultimate tensile strength, and impact fracture resistance with increase in the itaconate content. The mean values of surface hardness show no significant change with the addition of itaconates. The magnitude of the measured values indicates that the poly(methyl methacrylate) (PMMA) denture base material modified with itaconates could be developed into a less toxic, more environmentally and patient friendly product than commercial pure PMMA denture base material.
This study investigated the effect of shape, size, and surface modification of hydroxyapatite (HAP) fillers on the degree of conversion (DC) and mechanical properties of a model BisGMA/TEGDMA composite initially and after 4 weeks of storage. Ten percent of conventional glass fillers were replaced by HAP spheres (Sph), silicon-doped spheres (SphSi), whiskers (Wh), silicon-doped whiskers (WhSi), and nanosized HAP particles (Nano). Spheres were specifically structured agglomerates consisting of a central void and radially orientated primary particles, whereas whiskers were compact monocrystals. DC, Vickers hardness (HV), flexural strength (Fs), flexural modulus (Ef), compressive strength (Cs), and compressive modulus (Ec) were tested. There were no significant differences in the DC between all tested groups. HV decreased by 5.4-17% with the addition of HAP, while Fs increased by 13.9-29% except in Nano group (decrease by 13%). After storage, Sph and SphSi groups showed similar HV, Ef, Cs and Ec and higher Fs than the control. The fracture mode of HAP spheres was through the central void whereas whiskers showed longitudinal delamination, transverse, and mixed fractures. HAP spheres with or without silicon- doping have a potential to be part of the filler content of dental composites.
This article presents a literature review on the resin bond to zirconia ceramic. Modern esthetic dentistry has highly recognized zirconia, among other ceramic materials. Biocompatibility of zirconia, chemical and dimensional stability, excellent mechanical properties, all together could guarantee optimal therapeutical results in complex prosthodontic reconstruction. On the other hand, low thermal degradation, aging of zirconia as well as problematic bonding of zirconia framework to dental luting cements and tooth structures, opened the room for discussion concerning their clinical durability.The well known methods of mechanical and chemical bonding used on glass-ceramics are not applicable for use with zirconia. Therefore, under critical clinical situations, selection of the bonding mechanism should be focused on two important points: high initial bond strength value and long term bond strength between zirconia-resin interface. Also, this paper emphases the use of phosphate monomer luting cements on freshly air-abraded zirconia as the simplest and most effective way for zirconia cementation procedure today.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.