BERTOLINI, M. S. Use of CCB treated Pinus sp residues in particleboard production employing polyurethane resin based on castor oil. 2011. 128 f. Dissertação (Mestrado)

Tests simulating exposure to severe weather conditions have been relevant in seeking new applications for particleboard. This study aimed to produce particleboards with residues of CCB (chromium-copper-boron oxides) impregnated Pinus sp. and castor oil-based polyurethane resin, and to evaluate their performance before and after artificial accelerated aging. Panels were produced with different particle mass, resin content and pressing time, resulting eight treatments. Particles moisture and size distribution were determined, beyond panel physical and mechanical properties, according to NBR14810-3: 2006. After characterization, treatments B and G (small adhesive consumption and better mechanical performance, respectively) were chosen to artificial aging tests. Statistical results analysis showed best performances were achieved for waterproof aged samples, of both B and G treatments. As example, in treatment B, MOR and MOE values were 23 MPa and 2,297 MPa, samples before exposure; 26 MPa and 3,185 MPa, 32 MPa and 3,982 MPa for samples after exposure (non-sealed and sealed), respectively.

RESUMO -A utilização do preservante CCA (sais de cromo, cobre e arsênio) tem sido questionada devido ao impacto relacionado à dispersão, principalmente, do cobre e do arsênio para o ambiente, antes de sua completa fixação na madeira. Outra questão se relaciona à disposição indevida dos resíduos provenientes da madeira tratada, viabilizando a lixiviação devido à maior área passível desses rejeitos sujeita a tal fenômeno. Este trabalho teve como objetivo a produção de painéis de partículas, avaliando o efeito da adição de resíduos de Pinus sp. tratado com sais de cromo, cobre e arsênio (CCA), em associação com material da mesma espécie sem preservantes, além de alterações no teor de adesivo poliuretano à base de mamona empregado na produção. As propriedades dos painéis produzidos foram determinadas conforme recomendações da NBR 14810-3: 2006. Por meio de análise estatística, observou-se que a adição da madeira tratada proporcionou desempenho superior no inchamento em espessura (2 h), ao passo que esse insumo utilizado na mesma proporção que a madeira sem preservantes foi significante, obtendo os melhores resultados na adesão interna. Os módulos de ruptura e de elasticidade na flexão não sofreram influência das variações nos insumos utilizados nos painéis. Os painéis, em grande parte, apresentaram-se em conformidade com os principais requisitos nesse âmbito, mostrando a possibilidade da utilização dos referidos insumos na produção, além da obtenção de um produto com considerável apelo ambiental.Palavras-chave: Pinus sp.; Painéis aglomerados; Tratamento CCA. PARTICLEBOARDS USING WASTES FROM CCA-TREATED Pinus sp. AND RESIN FROM BIOMASS

Este trabalho objetivou avaliar a viabilidade da produção de painéis OSB feitos com espécies de madeira da caatinga do nordeste do Brasil - marmeleiro (Croton sonderianus Muell. Arg.), jurema-branca (Piptadenia stipulacea (Benth.) Ducke) e catanduva (Piptadenia moniliformis Benth.) - e resina poliuretana bicomponente derivada de mamona. As propriedades investigadas foram: densidade aparente; inchamento em espessura e absorção de água, ambos em 2 h e 24 h; módulo de elasticidade e resistência na flexão, na direção paralela e na direção perpendicular ao painel; adesão interna e arrancamento de parafuso em relação à face, conforme as normas europeias EN. Os resultados das propriedades físicas e mecânicas obtidas evidenciaram a possibilidade da produção em laboratório de painéis OSB com as três espécies analisadas, conforme valores médios e variabilidade de propriedades equivalentes às chapas fabricadas em escala industrial, além de comparados aos requisitos da norma EN 300 (EUROPEAN..., 2006) para painéis dos tipos OSB/3 e OSB/4. Pela análise de variância, os painéis OSB fabricados com strands de madeiras de catanduva apresentaram os melhores resultados para as propriedades mecânicas; para as físicas, os melhores desempenhos foram provenientes dos painéis feitos com madeira de marmeleiro e jurema-branca.

Wood toughness is a mechanical property of interest in structural design where the load impact must be considered, finding a strong application in bridges, however, not an integral part of the mechanical properties commonly investigated in the characterization of this material. This study aimed to investigate with the aid of variance analysis, the influence of growth ring orientation to obtain toughness for Angelim Saia (Parkia pendula), Eucalyptus grandis, Pinus elliottii and Corymbia citriodora wood species, considering three different positions, so that the orientation causes tensile strength in fibers near the pitch, near the bark, and in the radial direction. The results of the statistical analysis revealed that there was no significance in the orientation of the growth rings to obtain the toughness of the wood species investigated, where the highest values were for Corymbia citriodora and the least values were for Pinus elliottii.

ResumoOs painéis de partículas consistem em materiais compósitos com ampla gama de aplicações, dentre essas, na forma de pisos, em que a resistência à abrasão se configura como uma importante propriedade. Este trabalho objetivou investigar, com o auxílio da norma brasileira ABNT (2008), a resistência a abrasão (desgaste superficial) de painéis de partículas, fabricados com resíduos de madeira de Eucalyptus sp. para aplicação, na forma de pisos, em ambientes interiores. Os fatores investigados na fabricação dos painéis foram o tipo de resina (poliuretana a base de óleo de mamona; a ureia formaldeído), uso ou não de revestimento em verniz a base de poliéster e o número de ciclos para os ensaios de abrasão (1000; 1300; 1600), conduzindo a um planejamento fatorial completo com 12 tratamentos distintos. As respostas investigadas foram o desgaste por perda de massa, desgaste por perda de massa percentual, desgaste por perda de espessura e desgaste por perda de espessura percentual. Os resultados apresentaram valores de ciclos superiores às classes AC2 e AC3, chegando a 2700 ciclos, de acordo com a perda de massa. Da análise estatística, apenas o fator número de ciclos foi significativo nas propriedades investigadas, o que implica na equivalência de resultados para os demais fatores e interações investigadas. Palavras-chave: Painéis de partículas, resistência à abrasão, resinas. AbstractParticleboards consist of composite materials with a wide range of applications, among these, for floors, where abrasion is an important property. This research aimed to investigate, with the aid of the Brazilian standard ABNT (2008), abrasion resistance (surface wear) of particleboards manufactured with waste of Eucalyptus sp. wood for employment on indoor environments floors. The factors investigated in the manufacture of the panels were resin type (castor oil-based polyurethane resin, urea formaldehyde), the use or not of varnish coating based on polyester, and the number of cycles for the abrasion test (1000; 1300; 1600), leading to a full factorial design with 12 different treatments. The responses investigated were the wear mass loss, wear mass loss percentage, wear loss in thickness and wear loss percentage in thickness. The results showed higher number cycles values then AC2 and AC3 classes, reaching 2700 cycles according to the loss mass. In the statistical analysis, only the number of cycles factor was significant in the investigated properties, which implies equivalence results for the other factors and interactions evaluated.

No abstract

As dimensões de corpos-de-prova para caracterização da madeira são estabelecidas sempre buscando situações em que seja anulada a interferência do atrito nas medidas de deformação. A NBR 7190 (ABNT, 1997) -Anexo B adota corpos-de-prova para o ensaio de compressão paralela às fibras com relação 1:3 entre uma aresta da seção transversal (50 mm) e o comprimento, enquanto a COPANT 464 (COPANT, 1972) e ASTM D 143 (ASTM, 1982) estabelecem a de 1:4. Este trabalho objetivou determinar se as proporções 1:3, 1:4 e 1:5 nos corpos-de-prova, referentes aos comprimentos de 150, 200 e 250 mm, respectivamente, influenciam o E c0 obtido na compressão paralela às fibras. As análises foram realizadas nas espécies Canelão (Nectandra membranacea), Corymbia citriodora e Angelim (Vatairea sp.). Os valores de E c0 para as espécies citadas apresentaram-se estatisticamente equivalentes entre si, ao nível de 5% de significância, demonstrando que as variações nos comprimentos dos corpos-de-prova não afetaram esta propriedade.Palavras-chave: madeira -compressão paralela às fibras, módulo de elasticidade, comprimento de corpos-de-prova.