The purpose of this study was to test the hypothesis that mechanical polishing methods of ceramic surfaces allow similar superficial roughness to that of glazed surfaces. Twenty-five Vitadur Alpha ceramic discs (5 mm x 2 mm) were prepared according to the manufacturer's specifications. All specimens were glazed and randomly assigned to 5 groups (n=5), according to finishing and polishing protocols: G1: glazed (control); G2: diamond bur finishing; G3: G2 + silicon rubber tip polishing; G4: G3 + felt disc/diamond polishing paste; G5: G3 + felt disc impregnated with fine-particle diamond paste. Next, surface roughness means (Ra - microm) were calculated. Qualitative analysis was made by scanning electron microscopy. Surface roughness data were submitted to ANOVA and Tukey's test at 5% significance level. G1 and G4 were statistically similar (p>0.05). G2 presented the highest roughness means (p<0.05) followed by groups G3, G5, G4 and G1 in a decreasing order. The hypothesis was partially confirmed as only the mechanical polishing (G4) produced similar superficial roughness to that of surface glazing, although finishing and polishing are technically critical procedures.
ResumoIntrodução: Um novo design de pilar para implantes dentários está disponível com a possibilidade de melhorar a estética sem comprometer a resistência mecânica, usando blocos cerâmicos perfurados para CAD/CAM. Objetivo: Este estudo avaliou a influência da combinação de diferentes materiais cerâmicos para coroa e para pilar híbrido na distribuição de tensões de prótese sobre implante hexágono externo. Método: Zircônia, dissilicato de lítio e cerâmica híbrida foram avaliados, totalizando 9 combinações de materiais para coroa e mesoestrutura. Para análise de elementos finitos, uma coroa monolítica cimentada sobre um pilar híbrido (mesoestrutura + base de titânio) foi modelada sobre um implante de hexágono externo. Os modelos foram exportados em formato STEP para o software de análise, e os materiais foram considerados isotrópicos, lineares, elásticos e homogêneos. Uma carga oblíqua (30°, 300N) foi aplicada no fundo da fossa central e a fixação do sistema ocorreu na base do osso. Resultado: Para a estrutura da coroa, os materiais flexíveis concentram menos tensão que os rígidos. Ao analisar o pilar híbrido, maiores valores de tensão foram observados quando feito com zircônia combinada com uma coroa de cerâmica híbrida. Em todas as combinações simuladas, a distribuição de tensões foi semelhante para o parafuso de fixação e o implante. Conclusão: Associar um material cerâmico com elevado módulo elástico para a coroa com um material de menor módulo elástico para o pilar híbrido resulta em menor concentração de tensão máxima principal, sugerindo um comportamento mecânico promissor para o sistema hexágono externo.Descritores: Cerâmica; análise de elementos finitos; implantes dentários; desenho do pilar-implante; materiais dentários. AbstractIntroduction: A new dental implant-abutment design is available with the possibility of improving aesthetic with no compromise of mechanical strength, using perforated CAD/CAM ceramic blocks. Objective: This study evaluated the influence of crown and hybrid abutment ceramic materials combination on the stress distribution of external hexagon implant supported prosthesis. Method: Zirconia, lithium disilicate and hybrid ceramic were evaluated, totaling 9 combinations of crown and mesostructure materials. For finite element analysis, a monolithic crown cemented over a hybrid abutment (mesostructure + titanium base) was modeled and screwed onto an external hexagon implant. Models were then exported in STEP format to analysis software, and the materials were considered isotropic, linear, elastic and homogeneous. An oblique load (30°, 300N) was applied to the central fossa bottom and the system's fixation occurred on the bone's base. Result: For crown structure, flexible materials concentrate less stress than rigid ones. In analyzing the hybrid abutment, it presented higher stress values when it was made with zirconia combined with a hybrid ceramic crown. The stress distribution was similar regarding all combinations for the fixation screw and implant. Conclusion: For external hexagon ...
Objetivo: avaliar as principais caracteristicas das cerâmicas odontológicas, cimentos resinosos, tratamentos de superfície e verificação dos seus devidos modos de falha, frente à literatura e suas respectivas utilizações clínicas. Material e Métodos: foi realizada uma busca bibliográfica nos principais bancos de dados de saúde PUBMED (www.pubmed.gov) e Scholar Google (www.scholar.google.com.br), no qual coletou-se trabalhos que foram publicados de 2002 a 2020. Foram inclusos estudos laboratoriais, relatos de casos, revisões sistemáticas e revisões de literatura, que fossem desenvolvidos em indivíduos vivos. Logo, foram excluídos artigos que não tratavam a respeito das caracteristicas das cerâmicas odontológicas, cimentos resinosos, tratamentos de superfície e verificação dos seus devidos modos de falha, frente à literatura e suas respectivas utilizações clínicas. Resultados: as cerâmicas podem ser classificadas em cerâmicas vítreas, cerâmicas policristalinas e as cerâmicas híbridas. Do mesmo modo que existem diferentes composições das cerâmicas e agentes de união, há também alguns protocolos de tratamento de superfície que se diferem de acordo com a escolha desses materiais. Conclusão: diversos sistemas cerâmicos estão disponíveis no mercado, fazendo com que os profissionais da área protética necessitem de uma constante reciclagem acerca das suas propriedades e indicações, visto que bons resultados não são devidos exclusivamente ao tipo de material utilizado, mas sim, à seleção do melhor material, tipo de preparo em conjunto à habilidade do profissional, cimentos resinosos, tratamentos de superfície e verificação dos seus devidos modos de falha. Nesse contexto, fazem-se necessários maiores estudos com relação às cerâmicas odontológicas e seu devido uso em um cenário clínico
After prolonged aging, discrete color changes can occur in zirconia, particularly when it is contact with the oral environment, as is the case of abutments and monolithic crowns. Thus, clinical and laboratory care should be taken to maintain surface integrity of zirconia, minimizing aging. (J Esthet Restor Dent 28:304-312, 2016).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.