The wetting and corrosion behavior of three bis(trifluoromethylsulfonyl)imide-based ionic liquids: 1-Dodecyl-3-methylimidazolium bis (trifluoromethylsulfonyl) ]/TiN resulted as the best IL-surface combination for a good wettability, due to the higher dispersion of the charge on the large size cation in this IL and the higher values of total and polar component of the surface free energy for this coating. Finally, SEM-EDS analysis determined that [N 1888 ][NTf 2 ]/ZrN was the best option in order to avoid corrosion problems. The evaporation of water, present as impurity in the ionic liquids, was found the main reason because of corrosion did not occur in the tests carried out at 100 ºC.
This paper studies the tribological behavior of the ionic liquid methyltrioctylammonium bis(trifluoromethylsulfonyl)imide ([N 1888 ][NTf 2 ]) as additive at different concentrations (1.25, 2.50, 3.75 and 5.00 wt%) in a polar base oil (diester). A tribometer using a ball-on-disk reciprocating configuration under fully flooded lubrication was used at a frequency of 15 Hz, at three different loads (40, 80 and 120 N), stroke length of 4 mm, and duration of 45 minutes. Worn surface on the disk was studied by confocal microscopy, SEM and XPS. Main results showed similar coefficient of friction for all lubricant samples; but different wear results were found at different loads, probably related with the chemical states found for fluorine on the worn surface and the temperature-dependent adsorption-desorption processes.
This is a PDF file of an unedited manuscript that has been accepted for publication. As a service to our customers we are providing this early version of the manuscript. The manuscript will undergo copyediting, typesetting, and review of the resulting galley proof before it is published in its final citable form. Please note that during the production process errors may be discovered which could affect the content, and all legal disclaimers that apply to the journal pertain. ] ionic liquid as neat lubricant in a steel-steel contact. A ball-on-disk reciprocating rig was used: firstly, at constant frequency (15 Hz) under both variable loads (40 to 120 N) and sliding distances (216, 324 and 432 m); and secondly, at different frequencies (10 to 30 Hz) and constant both load (80 N) and sliding distance (432 m). Slight friction variations and increasing wear with rising loads was found at constant frequency. Different behavior was found at constant load. The tribofilm thickness formed on the worn surface was closely related to testing conditions and controlled tribological behavior.
The corrosion behaviour and solubility of three bis (trifluoromethylsulfonyl) , as a component in a mixture with different base oils were analysed. Six polar oils suitable for use in lubrication were utilized as base oil. Solubility tests were performed by using turbidimetry, and corrosion was checked at 4 v/v% by examining the roughness and chemical composition of the surface after 21 days. The results showed that long carbon chains in the cation improve the solubility greatly in diesters and slightly in polyolesters. Corrosion was not detected at this concentration.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.