Vertical indium phosphide nanowires have been grown epitaxially on silicon (111) by metalorganic vapor-phase epitaxy. Liquid indium droplets were formed in situ and used to catalyze deposition. For growth at 350 degrees C, about 70% of the wires were vertical, while the remaining ones were distributed in the 3 other <111> directions. The vertical fraction, growth rate, and tapering of the wires increased with temperature and V/III ratio. At 370 degrees C and V/III equal to 200, 100% of the wires were vertical with a density of approximately 1.0 x 10(9) cm(-2) and average dimensions of 3.9 mum in length, 45 nm in base width, and 15 nm in tip width. X-ray diffraction and transmission electron microscopy revealed that the wires were single-crystal zinc blende, although they contained a high density of rotational twins perpendicular to the <111> growth direction. The room temperature photoluminescence spectrum exhibited one peak centered at 912 +/- 10 nm with a FWHM of approximately 60 nm.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.