Chitosan-reinforced starch-based biodegradable composite films were prepared by solution casting. The chitosan content in the films was varied from 20% to 80% (w/w). Tensile strength (TS) and tensile modulus (TM) of the starch-based composites were improved significantly with the addition of chitosan. Water vapor permeability (WVP) and oxygen transmission rate (OTR) of chitosan-reinforced starch-based films showed a significant reduction compared to native chitosan film and indicated better barrier properties to water vapor and oxygen. The water uptake of the films pointed out better hydrophobic character due to the incorporation of chitosan in starch-based films. Thermal stability was also found to increase with the addition of chitosan in starch-based films and was confirmed by thermogravimetric analysis (TGA) and differential thermal analysis (DTA). Fourier transform infrared (FT-IR) spectroscopy supported the molecular interactions due to the reinforcement of chitosan in starch-based films. Surface and interface morphologies of chitosan film and starch/chitosan composite film were examined by

No abstract

No abstract

No abstract

Acrylamide (AAm)/carboxymethyl cellulose (CMC) blend hydrogels have been prepared by the application of gamma radiation from C0-60 source at room temperature (27˚C). The preparation conditions such as effect of CMC concentration and radiation dose on gel fraction and swelling behaviors were investigated. The maximum value of gel fraction is obtained at 25 kGy radiation dose. The swelling properties were investigated in distilled water, saline solution (NaCl) and buffer medium. The maximum swelling value of hydrogel was obtained at 48 hours in water. The swelling ratio of hydrogel decreased with increase in concentration of NaCl in swelling medium. In buffer, it was found that swelling ratio increased with increase in pH of medium.