The purpose of this study was to compare shear bond strength values obtained in human enamel and dentin with the values obtained in bovine teeth using two adhesive systems with different actions. Forty human tooth half-crowns and forty bovine tooth crowns were flattened to a minimum plain area of 5 mm in diameter. The samples were divided in four groups of 20 specimens each: 1) human enamel; 2) bovine enamel; 3) human dentin; 4) bovine dentin. The samples of each group were divided in 2 subgroups of 10 samples each, according to the adhesive system used: 1) Scotchbond Multi-Purpose (SBMP); and 2) Clearfil Liner Bond 2V (CLB2V) applied according to the manufacturer's recommendations. Afterwards, restorations of Z100 composite with cylindrical shape (4 mm diameter x 5 mm height) were made using a metallic mold to submit the samples to shear bond testing on an Instron universal testing machine, at a crosshead speed of 0.5 mm/min. The data were submitted to ANOVA and Tukey's test (5%). In enamel, there was no statistical difference between bovine and human teeth for SBMP (7.36 MPa, human; 8.24 MPa, bovine), nor for CLB2V (10.01 MPa, human; 7.95, bovine). In dentin, SBMP showed a statistically lower mean on human dentin (7.01 MPa) than on bovine dentin (11.74 MPa). For CLB2V, there was no statistical difference between human (7.43 MPa) and bovine (9.27 MPa) substrates.
Fracture load of the three ceramic systems was found to be influenced by ceramic composition. Moreover, cement and fatigue condition influenced the fracture loads of the crown specimens evaluated in this study.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.