Functionally graded scaffold (FGS) is designed to mimic the morphology, mechanical and biological properties of natural bone closely. Porosity variation strategy between different regions in FGS plays a crucial role in influencing its mechanical and biological performance. A combination of modeling tool and scripting language can effectively enhance the ability to optimize FGS designs. This study was aimed at determining the effect of porosity variation strategy on the mechanical performance and permeability of the as-built and as-heat-treated FGSs. Ti-6Al-4V FGSs with sizes of 10×10×15 mm and diamond lattice structures were designed and fabricated by means of selective laser melting. A wide range of porosities in the FGSs (38~75%) were achieved by applying six different porosity variation strategies. The elastic modulus (3.7~5.7 GPa) and yield strength (27.1~84.7 MPa) of the as-built FGSs were found to vary between the corresponding mechanical properties of cancellous bone and cortical bone. Heat treatment reduced the strengths by 13~56%. Porosity variation strategy strongly affected the deformation behavior and failure mechanisms of the FGSs. The sigmoid function-controlled FGSs showed gradual failure behavior and
Laser powder bed fusion (LPBF) is being increasingly used in the fabrication of complex-shaped structure parts with high precision. It is easy to form martensitic microstructure in Ti-6Al-4V alloy during manufacturing. Pre-heating the powder bed can enhance the thermal field produced by cyclic laser heating during LPBF, which can tailor the microstructure and further improve the mechanical properties. In the present study, all the Ti-6Al-4V alloy samples manufactured by LPBF at different powder bed temperatures exhibit a near-full densification state, with the densification ratio of above 99.4%. When the powder bed temperature is lower than 400 °C, the specimens are composed of a single α′ martensite. As the temperature elevates to higher than 400 °C, the α and β phase precipitate at the α′ martensite boundaries by the diffusion and redistribution of V element. In addition, the α/α′ lath coarsening is presented with the increasing powder bed temperature. The specimens manufactured at the temperature lower than 400 °C exhibit high strength but bad ductility. Moreover, the ultimate tensile strength and yield strength reduce slightly, whereas the ductility is improved dramatically with the increasing temperature, when it is higher than 400 °C.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.