We have performed neutron diffraction isotopic substitution experiments on aerodynamically levitated droplets of CaSiO(3), to directly extract intermediate and local structural information on the Ca environment. The results show a substantial broadening of the first Ca-O peak in the pair distribution function of the melt compared to the glass, which comprises primarily of 6- and 7-fold coordinated Ca-polyhedra. The broadening can be explained by a redistribution of Ca-O bond lengths, especially toward longer distances in the liquid. The first order neutron difference function provides a test of recent molecular dynamics simulations and supports the MD model which contains short chains or channels of edge shared Ca-octahedra in the liquid state. It is suggested that the polymerization of Ca-polyhedra is responsible for the fragile viscosity behavior of the melt and the glass forming ability in CaSiO(3).

The structure of molten Fe 2 SiO 4+x has been studied using both high-energy x-ray diffraction and Fe Kedge x-ray absorption near-edge structure (XANES) spectroscopy, combined with aerodynamic levitation and laser beam heating. A wide range of Fe 3+ contents were accessed by varying the levitation and atmospheric gas composition. Diffraction measurements were made in the temperature (T) and oxygen partial pressure ranges 1624(21) < T < 2183(94) K (uncertainties in parentheses) and-5.6(3) < ΔFMQ < +2.8(5) log units (relative to the Fayalite-Magnetite-Quartz buffer). Iron K-edge XANES measurements covered the ranges 1557(33) < T < 1994(36) K and-2.1(3) < ΔFMQ < +4.4(3) log units. Fe 3+ contents, x = Fe 3+ /ΣFe, estimated directly from the pre-edge peaks of the XANES spectra varied between 0.15(1) and 0.40(2). While these agree in some cases with semi-empirical models, notable discrepancies are discussed in the context of the limitations in both the models and in the calibrations used to derive oxidation state from XANES spectra. XANES pre-edge peak areas imply average Fe-O coordination numbers, n FeO , close to 5 for all Fe 3+ /ΣFe. Diffraction measurements yielded values of 4.4(2) < n FeO <

View the article online for updates and enhancements.

No abstract

No abstract