All known materials wear under extended mechanical contacting. Superlubricity may present solutions, but is an expressed mystery in C-based materials. We report negative wear of carbon nitride films; a wear-less condition with mechanically induced material inflation at the nanoscale and friction coefficient approaching ultralow values (0.06). Superlubricity in carbon nitride is expressed as C-N bond breaking for reduced coupling between graphitic-like sheets and eventual N desorption. The transforming surface layer acts as a solid lubricant, whereas the film bulk retains its high elasticity. The present findings offer new means for materials design at the atomic level, and for property optimization in wear-critical applications like magnetic reading devices or nanomachines.
Low-temperature growth of low friction wear-resistant amorphous carbon nitride thin films by mid-frequency, high power impulse, and direct current magnetron sputtering, Journal of Vacuum Science & Technology. A, 2015, 33(5) The potential of different magnetron sputtering techniques for the synthesis of low friction and wear resistant amorphous carbon nitride (a-CN x ) thin films onto temperature-sensitive AISI52100 bearing steel, but also Si(001) substrates was studied. Hence, a substrate temperature of 150 C was chosen for the film synthesis. The a-CN x films were deposited using mid-frequency magnetron sputtering (MFMS) with an MF bias voltage, high power impulse magnetron sputtering (HiPIMS) with a synchronized HiPIMS bias voltage, and direct current magnetron sputtering (DCMS) with a DC bias voltage. The films were deposited using a N 2 /Ar flow ratio of 0.16 at the total pressure of 400 mPa. The negative bias voltage, V s , was varied from 20 to 120 V in each of the three deposition modes. The microstructure of the films was characterized by high-resolution transmission electron microscopy and selected area electron diffraction, while the film morphology was investigated by scanning electron microscopy. All films possessed an amorphous microstructure, while the film morphology changed with the bias voltage. Layers grown applying the lowest substrate bias of 20 V exhibited pronounced intercolumnar porosity, independent of the sputter technique. Voids closed and dense films are formed at V s ! 60 V, V s ! 100 V, and V s ¼ 120 V for MFMS, DCMS, and HiPIMS, respectively. X-ray photoelectron spectroscopy revealed that the nitrogen-to-carbon ratio, N/C, of the films ranged between 0.2 and 0.24. Elastic recoil detection analysis showed that Ar content varied between 0 and 0.8 at. % and increased as a function of V s for all deposition techniques. All films exhibited compressive residual stress, r, which depends on the growth method; HiPIMS produces the least stressed films with values ranging between À0.4 and À1.2 GPa for all V s , while CN x films deposited by MFMS showed residual stresses up to À4.2 GPa. Nanoindentation showed a significant increase in film hardness and reduced elastic modulus with increasing V s for all techniques. The harder films were produced by MFMS with hardness as high as 25 GPa. Low friction coefficients, between 0.05 and 0.06, were recorded for all films. Furthermore, CN x films produced by MFMS and DCMS at V s ¼ 100 and 120 V presented a high wear resistance with wear coefficients of k 2.3 Â 10 À5 mm 3 /Nm. While all CN x films exhibit low friction, wear depends strongly on the structural and mechanical characteristics of the films. The MFMS mode is best suited for the production of hard CN x films, although high compressive stresses challenge the application on steel substrates. Films grown in HiPIMS mode provide adequate adhesion due to low residual stress values, at the expense of lower film hardness. Thus, a relatively wide mechanical property envelope is presented for CN x films, ...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.