In searching for solutions to reduce battery weight for military applications, films of hexanoyl chitosan/polystyrene containing ) and titanium oxide were prepared using filler were used, which are untreated TiO 2 and on the structural and electrical behavior of the prepared electrolyte systems has been investigated by using X-ray and impedance spectroscopy, respectively. The ac conductivity was calculated rmula in the temperature range from 283 K to 353 K. The SO 3 -TiO 2 and can be interpreted based on the correlated hexanoyl chitosan; polystyrene; composite polymer electrolytes.
Mixed metallic oxides are getting increasing attention as novel electrode materials for energy conversion devices. However, low mixed ionic-electronic conductivity and high operating temperature hamper the practical applications of these devices. This study reports an effective strategy to improve the conductivity and performance of the fuel cell at low temperature by partially incorporating graphene in the Li0.1Cu0.2Zn0.7-oxide (LCZ) composite. The proposed cathode material is synthesized via the cost effective conventional solid-state route. Graphene incorporated LCZ shows excellent performance, which is attributed to the favorable charge transport paths offering low area-specific resistance. An X-ray diffractometer (XRD) and scanning electron microscope (SEM) are employed for microstructural and surface morphological analyses, respectively. Electrical conductivities of all the materials are determined by the DC four probe method, and interestingly, LCZ-1.5% graphene exhibits an excellent conductivity of 3.5 S/cm in air atmosphere at a temperature of 450 °C with a minimum value of 0.057 Ωcm2 area-specific resistance (ASR) that demonstrates significantly good performance. Moreover, the three-layer fuel cell device is fabricated using sodium carbonated Sm0.2Ce0.8O (NSDC) as an electrolyte, which can operate at low temperatures exhibiting open circuit voltage 0.95 V and shows a peak power density, i.e., 267.5 mW/cm2 with hydrogen as the fuel.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.