A biorenewable polymer is synthesized via a green process using the RAFT principle for the first time in supercritical CO2 at 300 bar and 80 °C. α‐Methylene‐γ‐butyrolactone polymers of various chain lengths and molecular weights are obtained. The molecular weights vary from 10 000 up to 20 000 with low polydispersity indexes (PDI <1.5). Furthermore, the monomer conversion in supercritical CO2 is substantially higher, respectively 85% for ScCO2 compared to ≈65% for polymerizations conducted in dimethyl formamide (DMF) solvent. Chain extensions are carried out to confirm the livingness of the formed polymers in ScCO2. This opens up future possibilities of the formation of different polymer architectures in ScCO2. The polymers synthesized in ScCO2 have glass transition temperature (Tg) values ranging from 155 up to 190 °C. However, the presence of residual monomer encapsulated inside the formed polymer matrix affects the glass transition of the polymer that is lowered by increasing monomer concentrations. Hence, additional research is required to eliminate the remaining monomer concentration in the polymer matrix in order to arrive at the optimal Tg.
A solvent-free route of initiated chemical vapor deposition (iCVD) was used to synthesize a bio-renewable poly(α-Methylene-γ-butyrolactone) (PMBL) polymer. α-MBL, also known as tulipalin A, is a bio-based monomer that can be a sustainable alternative to produce polymer coatings with interesting material properties. The produced polymers were deposited as thin films on three different types of substrates—polycarbonate (PC) sheets, microscopic glass, and silicon wafers—and characterized via an array of characterization techniques, including Fourier-transform infrared (FTIR), proton nuclear magnetic resonance spectroscopy (1H NMR), ultraviolet visible spectroscopy (UV–vis), differential scanning calorimetry (DSC), size-exclusion chromatography (SEC), and thermogravimetric analysis (TGA). Optically transparent thin films and coatings of PMBL were found to have high thermal stability up to 310 °C. The resulting PMBL films also displayed good optical characteristics, and a high glass transition temperature (Tg~164 °C), higher than the Tg of its structurally resembling fossil-based linear analogue-poly(methyl methacrylate). The effect of monomer partial pressure to monomer saturation vapor pressure (Pm/Psat) on the deposition rate was investigated in this study. Both the deposition rate and molar masses increased linearly with Pm/Psat following the normal iCVD mechanism and kinetics that have been reported in literature.
Solid state nuclear magnetic resonance (ssNMR) is a powerful and attractive characterization method for obtaining insights into the chemical structure and dynamics of a wide range of materials. Current interest in cellulose-based materials, as sustainable and renewable natural polymer products, requires deep investigation and analysis of the chemical structure, molecular packing, end chain motion, functional modification, and solvent–matrix interactions, which strongly dictate the final product properties and tailor their end applications. In comparison to other spectroscopic techniques, on an atomic level, ssNMR is considered more advanced, especially in the structural analysis of cellulose-based materials; however, due to a dearth in the availability of a broad range of pulse sequences, and time consuming experiments, its capabilities are underestimated. This critical review article presents the comprehensive and up-to-date work done using ssNMR, including the most advanced NMR strategies used to overcome and resolve the structural difficulties present in different types of cellulose-based materials.
Solid-state NMR has proven to be a versatile technique for studying the chemical structure, 3D structure and dynamics of all sorts of chemical compounds. In nanotechnology and particularly in thin films, the study of chemical modification, molecular packing, end chain motion, distance determination and solvent-matrix interactions is essential for controlling the final product properties and applications. Despite its atomic-level research capabilities and recent technical advancements, solid-state NMR is still lacking behind other spectroscopic techniques in the field of thin films due to the underestimation of NMR capabilities, availability, great variety of nuclei and pulse sequences, lack of sensitivity for quadrupole nuclei and time-consuming experiments. This article will comprehensively and critically review the work done by solid-state NMR on different types of thin films and the most advanced NMR strategies, which are beyond conventional, and the hardware design used to overcome the technical issues in thin-film research.
Three zeolites (H‐Beta, H‐ZSM‐5 and H‐Y) were synthesized in the form of binder‐free macroscopic beads (d=215–840 μm) using a hydrothermal method employing anion‐exchange resin beads as hard template. The beads obtained after removal of the hard template by calcination consisted of crystalline zeolite domains connected with each other to form a hierarchical porous network in which the zeolitic micropores are accessible through meso‐ and macropores, as proven by characterization with XRD, N2 physisorption, SEM, and TEM. The composition, the nature and amount of acid sites and the degree of hydrophobicity of these beads were investigated by means of XRF, solid‐state NMR, pyridine‐FTIR and TGA. The zeolite beads were tested as heterogeneous catalysts in the Friedel‐Crafts acylation of anisole with acetic anhydride to produce para‐methoxyacetophenone. H‐Beta‐Beads displayed the best catalytic performance with 95 % conversion of acetic anhydride and 76 % yield of para‐methoxyacetophenone in a batch reactor test (90 °C, 6 h). Next, the catalytic performance of H‐Beta‐Beads was compared in both batch and continuous‐flow mode to extrudates prepared by mixing zeolite Beta powder with either kaolin or bentonite binders. H‐Beta‐Beads outperformed the extrudates in batch‐mode reactions and could be reused in multiple runs without discernible loss of activity. In the continuous‐flow test, H‐Beta‐Beads demonstrated higher average activity but deactivated more rapidly than the extrudates.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.