Wire arc additive manufacturing is currently rising as the main focus of research groups around the world. This is directly visible in the huge number of new papers published in recent years concerning a lot of different topics. This review is intended to give a proper summary of the international state of research in the area of wire arc additive manufacturing. The addressed topics in this review include but are not limited to materials (e.g., steels, aluminum, copper and titanium), the processes and methods of WAAM, process surveillance and the path planning and modeling of WAAM. The consolidation of the findings of various authors into a unified picture is a core aspect of this review. Furthermore, it intends to identify areas in which work is missing and how different topics can be synergetically combined. A critical evaluation of the presented research with a focus on commonly known mechanisms in welding research and without a focus on additive manufacturing will complete the review.
The supply and processing of materials for highly stressed components are usually cost-intensive. Efforts to achieve cost and resource efficiency lead to more complex structures and contours. Additive manufacturing steps for component repair and production offer significant economic advantages. Machining needs to be coordinated with additive manufacturing steps in a complementary way to produce functional surfaces suitable for the demands. Regarding inhomogeneity and anisotropy of the microstructure and properties as well as production-related stresses, a great deal of knowledge is still required for efficient use by small- and medium-size enterprises, especially for the interactions of subsequent machining of these difficult-to-machine materials. Therefore, investigations on these influences and interactions were carried out using a highly innovative cost-intensive NiCrMo alloy (IN725). These alloys are applied for claddings as well as for additive component manufacturing and repair welding using gas metal arc welding processes. For the welded specimens, the adequate solidification morphology, microstructure and property profile were investigated. The machinability in terms of finishing milling of the welded surfaces and comparative analyses for ultrasonic-assisted milling processes was examined focussing on surface integrity. It was shown that appropriate cutting parameters and superimposed oscillating of the milling tool in the direction of the tool rotation significantly reduce the mechanical loads for tool and workpiece surface. This contributes to ensure a high surface integrity, especially when cutting has to be carried out without cooling lubricants.
High entropy alloys (HEAs) are among of the most promising new metal material groups. The achievable properties can exceed those of common alloys in different ways. Due to the mixture of five or more alloying elements, the variety of high entropy alloys is fairly huge. The presented work will focus on some first insights on the weldability and the wear behavior of vanadium carbide precipitation Cr27.5Co14Fe22Mo22Ni11.65V2.85 HEA. The weldability should always be addressed in an early stage of any alloy design to avoid welding-related problems afterwards. The cast Cr27.5Co14Fe22Mo22Ni11.65V2.85 HEA has been remelted using a TIG welding process and the resulting microstructure has been examined. The changes in the microstructure due to the remelting process showed little influence of the welding process and no welding-related problems like hot cracks have been observed. It will be shown that vanadium carbides or vanadium-rich phases precipitate after casting and remelting in a two phased HEA matrix. The hardness of the as cast alloy is 324HV0.2 and after remelting the hardness rises to 339HV0.2. The wear behavior can be considered as comparable to a Stellite 6 cobalt base alloy as determined in an ASTM G75 test. Overall, the basic HEA design is promising due to the precipitation of vanadium carbides and should be further investigated.
The present investigations on generative manufacturing using metallic materials pursue the idea of transferring the microscopic structural morphology of a dual-phase steel in modified form to the macroscopic level. The aim is to be able to join materials of different lattice modifications and to combine their positive properties. This applies in particular to the combination of high tensile strength and good formability. For this investigation, a specimen was created from a high-strength ferritic/martensitic (25%) and an austenitic (75%) material with a defined welding sequence. The specimen was deliberately manufactured anisotropically using welding layers in order to quantify its properties. Tensile tests were performed on specimens with different weld seam orientations to determine the direction-dependent properties. As can be proven by the results, the application of welding processes with different materials results in an anisotropic behaviour in generative manufacturing. With regard to tensile strength and elongation, there is an integral value of the mechanical-technological properties of both base materials. The existing anisotropy can be utilized with regard to the design by adapting the alignment of the weld layers to the load.
In this study, the monotonic and cyclic material properties of steel material of medium static strength produced additively in the wire arc additive manufacturing (WAAM) process were investigated. This investigated material is expected to be particularly applicable to the field of mechanical engineering, for which practical applications of the WAAM process are still pending and for which hardly any characteristic values can be found in the literature so far. The focus of the investigation was, on the one hand, to determine how the material characteristics are influenced by the load direction in relation to the layered structure and, on the other hand, how they are affected by different interlayer temperatures. For this purpose, monotonic tensile tests were carried out at room temperature as well as at elevated temperatures, and the cyclic material properties were determined. In addition, the hardness of the material and the residual stresses induced during production were measured and compared. In addition to the provision of characteristic properties for the investigated material, it was aimed to determine the extent to which the interlayer temperature influences the strength characteristics, since this can have a considerable influence on the production times and, thus, the economic efficiency of the process.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.