To study the encapsulation method for heat dissipation of high brightness organic light emitting diode (OLED), red emitting OLED of ITO (150 ㎚) / 2-TNATA (50 ㎚) / NPB (30 ㎚) / Alq3 : 1 vol.% Rubrene (30 ㎚) / Alq3 (30 ㎚) / LiF (0.7 ㎚) / Al (200 ㎚) structure was fabricated, which on Alq3 (150 ㎚) / LiF (150 ㎚) as buffer layer and Al as protective layer was deposited to protect the damage of OLED, and subsequently it was encapsulated using attaching film and metal sheet. The current density, luminance and power efficiency was improved according to thickness of Al protective layer. The emission spectrum and the Commission International de L'Eclairage (CIE) coordinate did not have any effects on encapsulation process using attaching film and metal sheet The lifetime of encapsulated OLED using attaching film and metal sheet was 307 hours in 1,200 ㎚ Al thickness, which was increased according to thickness of Al protective layer, and was improved 7% compared with 287 hours, lifetime of encapsulated OLED using attaching film and flat glass. As a result, it showed the improved current density, luminance, power efficiency and the long lifetime, because the encapsulation method using attaching film and metal sheet could radiate the heat on OLED effectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.