When pyridine chemisorbed on silica–alumina was evacuated at 350°C, the 1460 cm−1 band due to Lewis-bound pyridine (LPY) remained while the 1540 cm−1 band due to Brønsted-bound pyridine (BPY) completely disappeared. This disappearance of the BPY band was revealed to accompany a loss of the Brønsted acid sites themselves besides their liberation. However, the lost Brønsted acid sites were regenerated by allowing the sample to stand overnight at 110°C. Thus, strong Lewis acid sites of silica–alumina were able to be selectively poisoned by pyridine without any damage to the Brønsted acid sites. By poisoning catalysts in situ by controlled amounts in this way, the nature of the active site was investigated for polymerization of propylene or cis-2-butene at a low temperature of 30 °C. The initial activity declined sharply as the extent of pyridine poisoning of the Lewis acid sites increased. Therefore, it was concluded that strong Lewis acid sites (25–30% of the total Lewis acid content) were active in polymerization over silica–alumina.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.