Fe-doped LiTaO3 thin films with a low and high Fe concentration (labeled as LTO:Fe-LC and LTO:Fe-HC, respectively) were deposited by magnetron sputtering from two home-made targets. The dopant directly influenced the crystalline structure of the LiTaO3 thin films, causing the contraction of the unit cell, which was related to the incorporation of Fe3+ ions into the LiTaO3 structure, which occupied Li positions. This substitution was corroborated by Raman spectroscopy, where the bands associated with Li-O bonds broadened in the spectra of the samples. Magnetic hysteresis loops, zero-field cooling curves, and field cooling curves were obtained in a vibrating sample magnetometer. The LTO:Fe-HC sample demonstrates superparamagnetic behavior with a blocking temperature of 100 K, mainly associated with the appearance of Fe clusters in the thin film. On the other hand, a room temperature ferromagnetic behavior was found in the LTO:Fe-LC layer where saturation magnetization (3.80 kAm−1) and magnetic coercivities were not temperature-dependent. Moreover, the crystallinity and morphology of the samples were evaluated by X-ray diffraction and scanning electron microscopy, respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.