The study of hydrogen evolution reaction and oxygen evolution reaction electrocatalysts for water electrolysis is a developing field in which noble metal-based materials are commonly used. However, the associated high cost and low abundance of noble metals limit their practical application. Non-noble metal catalysts, aside from being inexpensive, highly abundant and environmental friendly, can possess high electrical conductivity, good structural tunability and comparable electrocatalytic performances to state-of-the-art noble metals, particularly in alkaline media, making them desirable candidates to reduce or replace noble metals as promising electrocatalysts for water electrolysis. This article will review and provide an overview of the fundamental knowledge related to water electrolysis with a focus on the development and progress of non-noble metal-based electrocatalysts in alkaline, polymer exchange membrane and solid oxide electrolysis. A critical analysis of the various catalysts currently available is also provided with discussions on current challenges and future perspectives. In addition, to facilitate future research and development, several possible research directions to overcome these challenges are provided in this article.

An evolution panorama of morphology and surface orientation of high-voltage spinel LiNi(0.5)Mn(1.5)O4 cathode materials synthesized by the combination of the microwave-assisted hydrothermal technique and a postcalcination process is presented. Nanoparticles, octahedral and truncated octahedral particles with different preferential growth of surface orientations are obtained. The structures of different materials are studied by X-ray diffraction (XRD), Raman spectroscopy, X-ray absorption near edge spectroscopy (XANES), and transmission electron microscopy (TEM). The influence of various morphologies (including surface orientations and particle size) on kinetic parameters, such as electronic conductivity and Li(+) diffusion coefficients, are investigated as well. Moreover, electrochemical measurements indicate that the morphological differences result in divergent rate capabilities and cycling performances. They reveal that appropriate surface-tailoring can satisfy simultaneously the compatibility of power capability and long cycle life. The morphology design for optimizing Li(+) transport and interfacial stability is very important for high-voltage spinel material. Overall, the crystal chemistry, kinetics and electrochemical performance of the present study on various morphologies of LiNi(0.5)Mn(1.5)O4 spinel materials have implications for understanding the complex impacts of electrode interface and electrolyte and rational design of rechargeable electrode materials for lithium-ion batteries. The outstanding performance of our truncated octahedral LiNi(0.5)Mn(1.5)O4 materials makes them promising as cathode materials to develop long-life, high energy and high power lithium-ion batteries.

A general large-scale synthesis of single-crystalline and uniform CeO 2 nanorods was first realized without templates by a precipitation method at room temperature and pressure. Such nanorods have an aspect ratio of ca. 3 nm with a diameter of ca. 8 nm and a large BET specific area of 128.2 m 2 / g. On the basis of this, the controlled conversion of the asprepared nanorods into nanotubes, nanowires, and nanocubes through hydrothermal reactions has been realized. Further experimental results show that the growth of nanorods is a function of the base concentration, temperature, and time. In addition, particle size measurements demonstrate that the primary nanorods grow by Ostwald ripening. It is found that CeO 2 growth is faster at higher base concentra-

In this study, a facile one-pot process for the synthesis of hierarchical VS2/graphene nanosheets (VS2/GNS) composites based on the coincident interaction of VS2 and reduced graphene oxide (rGO) sheets in the presence of cetyltrimethylammonium bromide is developed for the first time. The nanocomposites possess a hierarchical structure of 50 nm VS2 sheets in thickness homogeneously anchored on graphene. The VS2/GNS nanocomposites exhibit an impressive high-rate capability and good cyclic stability as a cathode material for Li-ion batteries, which retain 89.3% of the initial capacity 180.1 mAh g(-1) after 200 cycles at 0.2 C. Even at 20 C, the composites still deliver a high capacity of 114.2 mAh g(-1) corresponding to 62% of the low-rate capacity. Expanded studies show that VS2/GNS, as an anode material, also has a good reversible performance with 528 mAh g(-1) capacity after 100 cycles at 200 mA g(-1). The excellent electrochemical performance of the composites for reversible Li+ storage should be attributed to the exceptional interaction between VS2 and GNS that enabled fast electron transport between graphene and VS2, facile Li-ion diffusion within the electrode. Moreover, GNS provides a topological and structural template for the nucleation and growth of two-dimensional VS2 nanosheets and acted as buffer matrix to relieve the volume expansion/contraction of VS2 during the electrochemical charge/discharge, facilitating improved cycling stability. The VS2/GNS composites may be promising electrode materials for the next generation of rechargeable lithium ion batteries.

Li(3)V(2)(PO(4))(3)/graphene nanocomposites have been firstly formed on reduced graphene sheets as cathode material for lithium batteries. The nanocomposites synthesized by the sol-gel process exhibit excellent high-rate and cycling stability performance, owing to the nanoparticles connected with a current collector through the conducting graphene network.