The series of sulfonated poly(arylene ether ketone) (SPAEK) block copolymers with controlled F-oligomer length bearing pendant diphenyl unit were synthesized via a polycondensation reaction. Sulfonation was verified by H NMR analysis to introduce sulfonic acid group selectively and intensively on the pendant diphenyl unit of polymer backbones. The SPAEK membranes fabricated by the solution casting approach were very transparent and flexible with the thickness of ∼50 μm. These membranes with different F-oligomer lengths were investigated to the physiochemical properties such as water absorption, dimensional stability, ion exchange capacity, and proton conductivity. As a result, the SPAEK membranes (X4.8Y8.8, X7.5Y8.8, and X9.1Y8.8) in accordance to increasing the length of hydrophilic oligomer showed excellent proton conductivity in range of 131-154 mS cm compared to Nafion-115 (131 mS cm) at 90 °C under 100% relative humidity (RH). Among the SPAEK membranes, proton conductivity of SPAEK X9.1Y8.8 (140.7 mS cm) is higher than that of Nafion-115 (102 mS cm) at 90 °C under 80% RH. The atomic force microscopy image demonstrated that number of ion transport channels is increased with increase in the length of hydrophilic oligomer in the main chains, and the morphology is proved to be related to the proton conductivity. The synthesized SPAEK membrane exhibited a maximum power density of 324 mW cm, which is higher than that of Nafion-115 (291 mW cm) at 60 °C under 100% RH.
Summary
Organic‐inorganic composite membranes were prepared by introducing silicon dioxide (SiO2) or functionalized SiO2 (ƒ‐SiO2) with various particle sizes into sulfonated poly (arylene ether ketone) (SPAEK) containing pendant groups, and the membrane was manufactured via directly casting which is a cost‐competitive method. The structure and morphology of the composite membranes were confirmed by 1H NMR, FT‐IR, XRD, and FE‐SEM analysis which demonstrated that inorganic nanofillers were successfully introduced. The FE‐SEM surface images showed that SiO2 and ƒ‐SiO2 particles were very well dispersed within the membrane sheets. The water uptake and swelling ratio of the composite membranes including SiO2 or ƒ‐SiO2 almost did not change when compared with the pristine SPAEK membrane. All fabricated membranes demonstrated good thermal/dimensional stabilities, robust mechanical behavior, and excellent proton conductivity. In particular, the SPAEK/ƒ‐SiO2 composite membranes exhibited improved ionic conductivity compared with the pristine membrane at 70% relative humidity (RH) due to hydrogen bonding between ─SO3H groups of functionalized inorganic filler and polymer backbone. Furthermore, the maximum power density of SPAEK/ƒ‐SiO2 reached as high as 273.11 mW cm−2 at 60°C under 70% RH. Therefore, the composite membranes with ƒ‐SiO2 testify to great potential as polymer electrolyte membrane.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.