This research is focused on the analysis of heat-affected sub-zones in 2 mm thick steel S960MC samples, with the aim of observing and evaluating the mechanical properties after exposure to temperatures corresponding to individual heat-affected sub-zones. Test samples were prepared using a Gleeble 3500 thermo-mechanical simulator. The samples were heated in the range from 550°C to 1350°C and were subsequently quickly cooled. The specimens, together with the base material, were then subjected to tensile testing, impact testing, and micro-hardness measurements in the sample cross-section, as well as evaluation of their microstructure. Fracture surfaces are investigated in samples after impact testing. The heat-affected sub-zones studied indicate high sensitivity to the thermal input of welding. There is a significant decrease in tensile strength and yield strength at temperatures around 550°C.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.