The dispersion behavior of graphene oxide in different organic solvents has been investigated. As-prepared graphite oxide could be dispersed in N, N-dimethylformamide, N-methyl-2-pyrrolidone, tetrahydrofuran, and ethylene glycol. In all of these solvents, full exfoliation of the graphite oxide material into individual, single-layer graphene oxide sheets was achieved by sonication. The graphene oxide dispersions exhibited long-term stability and were made of sheets between a few hundred nanometers and a few micrometers large, similar to the case of graphene oxide dispersions in water. These results should facilitate the manipulation and processing of graphene-based materials for different applications.

The preparation of solution-processable graphene from graphite oxide typically involves a hydrazine reduction step, but the use of such a reagent in the large-scale implementation of this approach is not desirable due to its high toxicity. Here, we compare the deoxygenation efficiency of graphene oxide suspensions by different reductants (sodium borohydride, pyrogallol, and vitamin C, in addition to hydrazine), as well as by heating the suspensions under alkaline conditions. In almost all cases, the degree of reduction attainable and the subsequent restoration of relevant properties (e.g., electrical conductivity) lag significantly behind those achieved with hydrazine. Only vitamin C is found to yield highly reduced suspensions in a way comparable to those provided by hydrazine. Stable suspensions of vitamin C-reduced graphene oxide can be prepared not only in water but also in common organic solvents, such as N,N-dimethylformamide (DMF) or N-methyl-2-pyrrolidone (NMP). These results open the perspective of replacing hydrazine in the reduction of graphene oxide suspensions by an innocuous and safe reductant of similar efficacy, thus facilitating the use of graphene-based materials for large-scale applications.

No abstract

No abstract

Graphene nanosheets produced in the form of stable aqueous dispersions by chemical reduction of graphene oxide and deposited onto graphite substrates have been investigated by atomic force and scanning tunneling microscopy (AFM/STM). The chemically reduced graphene oxide nanosheets were hardly distinguishable from their unreduced counterparts in the topographic AFM images. However, they could be readily discriminated through phase imaging in the attractive regime of tapping-mode AFM, probably because of differences in hydrophilicity arising from their distinct oxygen contents. The chemically reduced nanosheets displayed a smoothly undulated, globular morphology on the nanometer scale, with typical vertical variations in the subnanometer range and lateral feature sizes of approximately 5-10 nm. Such morphology was attributed to be the result of significant structural disorder in the carbon skeleton, which originates during the strong oxidation that leads to graphene oxide and remains after chemical reduction. Direct evidence of structural disorder was provided by atomic-scale STM imaging, which revealed an absence of long-range periodicity in the graphene nanosheets. Only structured domains a few nanometers large were observed instead. Likewise, the nanosheet edges appeared atomically rough and ill-defined, though smooth on the nanometer scale. The unreduced graphene oxide nanosheets could only be imaged by STM at very low tunneling currents (approximately 1 pA), being visualized in some cases with inverted contrast relative to the graphite substrate, a result that was attributed to their extremely low conductivity. Complementary characterization of the unreduced and chemically reduced nanosheets was carried out by thermogravimetric analysis as well as UV-visible absorption and X-ray photoelectron and Raman spectroscopies. In particular, the somewhat puzzling Raman results were interpreted to be the result of an amorphous character of the graphene oxide material.