Complex multiple-component semiconductor photocatalysts can be constructed that display enhanced catalytic efficiency via multiple charge and energy transfer, mimicking photosystems in nature. In contrast, the efficiency of single-component semiconductor photocatalysts is usually limited due to the fast recombination of the photogenerated excitons. Here, we report the design of an asymmetric covalent triazine framework as an efficient organic single-component semiconductor photocatalyst. Four different molecular donor-acceptor domains are obtained within the network, leading to enhanced photogenerated charge separation via an intramolecular energy transfer cascade. The photocatalytic efficiency of the asymmetric covalent triazine framework is superior to that of its symmetric counterparts; this was demonstrated by the visible-light-driven formation of benzophosphole oxides from diphenylphosphine oxide and diphenylacetylene.

Using time-resolved photoluminescence (TRPL) spectroscopy the exciton lifetime in a range of conjugated polymers is investigated. For poly(p-phenylenevinylene) (PPV)-based derivatives and a polyspirobifluorene copolymer (PSBF) we find that the exciton lifetime is correlated with the energetic disorder. Better ordered polymers exhibit a single exponential PL decay with exciton lifetimes of a few hundred picoseconds, whereas polymers with a larger degree of disorder show multiexponential PL decays with exciton lifetimes in the nanosecond regime. These observations are consistent with diffusion-limited exciton quenching at nonradiative recombination centers. The measured PL decay time reflects the time that excitons need to diffuse toward these quenching sites. Conjugated polymers with large energetic disorder and thus longer exciton lifetime also exhibit a higher photoluminescence quantum yield due to the slower exciton diffusion toward nonradiative quenching sites.

We show that the exciton transport and decay processes in two poly(p-phenylene vinylene) (PPV) based semiconducting polymers exhibit distinct temperature dependence based on the energetic disorder of the polymer.