Particle size control of colloidal mesoporous silica nanoparticles (CMPS) in a very wide range is quite significant for the design of CMPS toward various applications, such as catalysis and drug delivery. Various types of CMPS and their precursors (colloidal mesostructured silica nanoparticles (CMSS)) with different particle sizes (ca. 20-700 nm) were newly prepared from tetraalkoxysilanes with different alkoxy groups (Si(OR)4, R = Me, Et, Pr, and Bu) in the presence of alcohols (R'OH, R' = Me, Et, Pr, and Bu) as additives. CMSS with larger particle size were obtained by using tetrabutoxysilane (TBOS) and by increasing the amount of BuOH, which is explained by both the difference in the hydrolysis rates of tetraalkoxysilanes themselves and the effect of added alcohols on the hydrolysis rates of tetraalkoxysilanes. Larger amounts of alcohols with longer alkyl chains decrease the hydrolysis rates of tetraalkoxysilanes and the subsequent formation rates of silica species. Thus, the preferential particle growth of CMSS to nucleation occurs, and larger CMSS are formed. Highly dispersed CMPS were prepared by the removal of surfactants of CMSS by dialysis which can lead to the preparation of CMPS without aggregation. Therefore, the particle size control through the tuning of the hydrolysis rate of tetraalkoxysilanes can be conducted by a one-pot and easy approach. Even larger CMPS (ca. 700 nm in size) show relatively high dispersibility. This dispersibility will surely contribute to the design of materials both retaining nanoscale characteristics and avoiding various nanorisks.

Both the pore size and particle diameter of aqueous colloidal mesostructured/mesoporous silica nanoparticles (CMSS/CMPS) derived from tetrapropoxysilane were effectively and easily controlled by the addition of trialkylbenzenes (TAB). Aqueous highly dispersed CMPS with large pores were successfully obtained through removal of surfactants and TAB by a dialysis process. The pore size (from 4 nm to 8 nm) and particle diameter (from 50 nm to 380 nm) were more effectively enlarged by the addition of 1,3,5-triisopropylbenzene (TIPB) than 1,3,5-trimethylbenzene (TMB), and the enlargement did not cause the variation of the mesostructure and particle morphology. The larger molecular size and higher hydrophobicity of TIPB than TMB induce the incorporation of TIPB into micelles without the structural change. When TMB was used as TAB, the pore size of CMSS was also enlarged while the mesostructure and particle morphology were varied. Interestingly, when tetramethoxysilane and TIPB were used, CMSS with a very small particle diameter (20 nm) with concave surfaces and large mesopores were obtained, which may strongly be related to the initial nucleation of CMSS. A judicious choice of TAB and Si sources is quite important to control the mesostructure, size of mesopores, particle diameter, and morphology.

Colloidal mesoporous silica nanoparticles asymmetrically capped with non-porous phenylsilsesquioxane have been prepared by adding phenyltriethoxysilane to an aqueous dispersion of mesostructured silica-surfactant composite nanoparticles. The integration of colloidal stability, mesoporosity and the Janus structure is quite promising for materials design applicable in various fields, including catalysis, biomedicine and coatings.