The nanocrystals (NCs) of inorganic perovskites CsPbX3 and Cs4PbX6 (X = Cl, Br, I) are showing a great development potential due to their versatility of crystal structure. Here, we used a microchannel reactor to synthesize both CsPbBr3 NCs (CsPbBr3 NCs) and Cs4PbBr6 NCs with embedded CsPbBr3 (CsPbBr3/Cs4PbBr6 NCs). Via speed control of the precursor, ligands around the surface of NCs were effectively regulated by ethyl acetate, allowing the transformation from CsPbBr3 NCs to CsPbBr3/Cs4PbBr6 NCs in a short time, an outstanding stability of NCs, and a better crosslinking between NCs and polymer for the application of LEDs. Without any protection, the CsPbBr3/Cs4PbBr6 NCs, with a production rate of 28 mg min−1, retain more than 90% of the PL intensity after 84 d. Finally, the CsPbBr3/Cs4PbBr6 NCs were used to produce an LED device, and a wide color gamut of 122.8% NTSC or 91.7% Rec 2020 was attained.
We developed a microreactor with porous copper fibers for synthesizing nitrogen-doped carbon dots (N-CDs) with a high stability and photoluminescence (PL) quantum yield (QY). By optimizing synthesis conditions, including the reaction temperature, flow rate, ethylenediamine dosage, and porosity of copper fibers, the N-CDs with a high PL QY of 73% were achieved. The PL QY of N-CDs was two times higher with copper fibers than without. The interrelations between the copper fibers with different porosities and the N-CDs were investigated using X-ray photoelectron spectroscopy (XPS) and Fourier Transform infrared spectroscopy (FTIR). The results demonstrate that the elemental contents and surface functional groups of N-CDs are significantly influenced by the porosity of copper fibers. The N-CDs can be used to effectively and selectively detect Hg2+ ions with a good linear response in the 0~50 μM Hg2+ ions concentration range, and the lowest limit of detection (LOD) is 2.54 nM, suggesting that the N-CDs have great potential for applications in the fields of environmental and hazard detection. Further studies reveal that the different d orbital energy levels of Hg2+ compared to those of other metal ions can affect the efficiency of electron transfer and thereby result in their different response in fluorescence quenching towards N-CDs.
The ability to precisely obtain tunable spectrum of lead halide perovskite quantum dots (QDs) is very important for applications, such as in lighting and display. Herein, we report a microchannel reactor method for synthesis of CsPbBr3 QDs with tunable spectrum. By adjusting the temperature and velocity of the microchannel reactor, the emission peaks of CsPbBr3 QDs ranging from 520 nm to 430 nm were obtained, which is wider than that of QDs obtained in a traditional flask without changing halide component. The mechanism of photoluminescence (PL) spectral shift of CsPbBr3 QDs was investigated, the result shows that the supersaturation control enabled by the superior mass and heat transfer performance in the microchannel is the key to achieve the wide range of PL spectrum, with only a change in the setting of the temperature controller required. The wide spectrum of CsPbBr3 QDs can be applied to light-emitting diodes (LEDs), photoelectric sensors, lasers, etc.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.