Bone cement is used extensively in orthopedics to anchor prostheses to bone and fill voids. Incorporating bioactive glass into poly(methyl methacrylate) (PMMA)‐based bone cement could potentially improve its effectiveness for these tasks. This study characterizes the mechanical and degradation properties of composites containing PMMA‐based bone cement and particles of borate bioactive glass designated as 13‐93B3. Glass particles of size 5, 33, and 100 μm were mixed with PMMA bone cement to create composites containing 20, 30, and 40 wt % glass. Composites and a bone cement control were soaked in phosphate‐buffered saline. Compressive strength, Young's modulus, weight loss, water uptake, solution pH, and ionic concentrations were measured over 21 days. The compressive strengths of composites decreased over 21 days. Average Young's moduli of the composites remained below 3 GPa. Weight loss and water uptake of specimens did not exceed 2 and 6%, respectively. Boron concentrations and pH of all solutions increased over time, with higher glass weight fractions leading to higher pH values. Results demonstrated that the composite can sustain glass degradation and ionic release without compromising short‐term mechanical strength.

Introduction: Local delivery of antibiotics using bone cement as the delivery vehicle is an established method of managing implant-associated orthopedic infections. Various fillers have been added to cement to increase antibiotic elution, but they often do so at the expense of strength. This study evaluated the effect of adding a borate bioactive glass, previously shown to promote bone formation, on vancomycin elution from PMMA bone cement.Methods: Five cement composites were made: three loaded with borate bioactive glass along with 0, 1, and 5 grams of vancomycin and two without any glass but with 1 and 5 grams vancomycin to serve as controls. The specimens were soaked in PBS. Eluate of vancomycin was collected every 24 hours and analyzed by HPLC. Orthopedic-relevant mechanical properties of each composite were tested over time.Results: The addition of borate bioactive glass provided an increase in vancomycin release at Day 1 and an increase in sustained vancomycin release throughout the treatment period. An 87.6% and 21.1% increase in cumulative vancomycin release was seen for both 1g and 5g loading groups, respectively. Compressive strength of all composites remained above the weight-bearing threshold of 70 MPa throughout the duration of the study with the glass-containing composites showing comparable strength to their respective controls.Conclusion: The incorporation of borate bioactive glass into commercial PMMA bone cement can significantly increase the elution of vancomycin. The mechanical strength of the cement-glass composites remained above 70 MPa even after soaking for 8 weeks, suggesting their suitability for orthopedic weight-bearing applications.

Borate bioactive glass 13‐93B3 converts into an osteoconductive hydroxyapatite‐like material in a liquid medium. In this study, 13‐93B3 was incorporated into a commercial PMMA (poly(methyl methacrylate)) bone cement, and the conversion of the glass into a precipitate in solution was investigated with scanning electron microscopy, energy dispersive X‐ray spectroscopy, Fourier transform infrared (spectroscopy)—attenuated total reflection, and micro‐Raman spectroscopy. Glass particles of 5, 33, and 100 μm diameter were each mixed with the PMMA cement to create 20, 30, and 40% glass‐loaded composites. Precipitate formation was found to be a calcium‐deficient apatite partially substituted with magnesium ions that resembles native bone material and would ideally encourage bone growth better than stoichiometric hydroxyapatite. Composites of bone cement and 13‐93B3 show promise as a means of encouraging bone attachment to the surface of the bone cement.

Objectives The objective of this study was to characterize the effect of rifampin incorporation into poly(methyl methacrylate) (PMMA) bone cement. While incompatibilities between the two materials have been previously noted, we sought to identify and quantify the cause of rifampin’s effects, including alterations in curing properties, mechanical strength, and residual monomer content. Methods Four cement groups were prepared using commercial PMMA bone cement: a control; one with 1 g of rifampin; and one each with equimolar amounts of ascorbic acid or hydroquinone relative to the amount of rifampin added. The handling properties, setting time, exothermic output, and monomer loss were measured throughout curing. The mechanical strength of each group was tested over 14 days. A radical scavenging assay was used to assess the scavenging abilities of rifampin and its individual moieties. Results Compared with control, the rifampin-incorporated cement had a prolonged setting time and a reduction in exothermic output during polymerization. The rifampin cement showed significantly reduced strength and was below the orthopaedic weight-bearing threshold of 70 MPa. Based on the radical scavenging assay and strength tests, the hydroquinone structure within rifampin was identified as the polymerization inhibitor. Conclusion The incorporation of rifampin into PMMA bone cement interferes with the cement’s radical polymerization. This interference is due to the hydroquinone moiety within rifampin. This combination alters the cement’s handling and curing properties, and lowers the strength below the threshold for weight-bearing applications. Additionally, the incomplete polymerization leads to increased toxic monomer output, which discourages its use even in non-weight-bearing applications. Cite this article : G. A. Funk, E. M. Menuey, K. A. Cole, T. P. Schuman, K. V. Kilway, T. E. McIff. Radical scavenging of poly(methyl methacrylate) bone cement by rifampin and clinically relevant properties of the rifampin-loaded cement. Bone Joint Res 2019;8:81–89. DOI: 10.1302/2046-3758.82.BJR-2018-0170.R2.

Aims Poly(methyl methacrylate) (PMMA)-based bone cements are the industry standard in orthopaedics. PMMA cement has inherent disadvantages, which has led to the development and evaluation of a novel silorane-based biomaterial (SBB) for use as an orthopaedic cement. In this study we test both elution and mechanical properties of both PMMA and SBB, with and without antibiotic loading. Methods For each cement (PMMA or SBB), three formulations were prepared (rifampin-added, vancomycin-added, and control) and made into pellets (6 mm × 12 mm) for testing. Antibiotic elution into phosphate-buffered saline was measured over 14 days. Compressive strength and modulus of all cement pellets were tested over 14 days. Results The SBB cement was able to deliver rifampin over 14 days, while PMMA was unable to do so. SBB released more vancomycin overall than did PMMA. The mechanical properties of PMMA were significantly reduced upon rifampin incorporation, while there was no effect to the SBB cement. Vancomycin incorporation had no effect on the strength of either cement. Conclusion SBB was found to be superior in terms of rifampin and vancomycin elution. Additionally, the incorporation of these antibiotics into SBB did not reduce the strength of the resultant SBB cement composite whereas rifampin substantially attenuates the strength of PMMA. Thus, SBB emerges as a potential weight-bearing alternative to PMMA for the local delivery of antibiotics. Cite this article: Bone Joint Res 2021;10(4):277–284.