No abstract

Novel porous ZnO/ZnFe2O4/C octahedra with hollow interiors are fabricated by a facile self-sacrificing template method involving the refluxing synthesis of hollow, metal-organic framework octahedra in solution and subsequent thermal annealing in N2 . When evaluated as an anode material for lithium-ion batteries, these porous hollow ZnO/ZnFe2O4/C octahedra exhibit significantly enhanced electrochemical performances with high rate capability, high capacity, and excellent cycling stability.

S‐doped carbon is investigated as a high‐performance anode material for sodium‐ion batteries. Due to the introduction of a high‐content of S atoms, the as‐obtained S‐doped carbon shows an enlarged interlayer distance. As an anode, a high specific capacity of up to 303 mAh g−1 is achieved, even after 700 cycles at 0.5 A g−1.

Ni-based metal organic frameworks (Ni-MOFs) with unique hierarchical hollow ball-in-ball nanostructure were synthesized by solvothermal reactions. After successive carbonization and oxidation treatments, hierarchical NiO/Ni nanocrystals covered with a graphene shell were obtained with the hollow ball-in-ball nanostructure intact. The resulting materials exhibited superior performance as the anode in lithium ion batteries (LIBs): they provide high reversible specific capacity (1144 mAh/g), excellent cyclability (nearly no capacity loss after 1000 cycles) and rate performance (805 mAh/g at 15 A/g). In addition, the hierarchical NiO/Ni/Graphene composites demonstrated promising performance as anode materials for sodium-ion batteries (SIBs). Such a superior lithium and sodium storage performance is derived from the well-designed hierarchical hollow ball-in-ball structure of NiO/Ni/Graphene composites, which not only mitigates the volume expansion of NiO during the cycles but also provides a continuous highly conductive graphene matrix to facilitate the fast charge transfer and form a stable SEI layer.

Oxygen evolution reaction (OER) is a pivotal process in many energy conversion and storage techniques, such as water splitting, regenerative fuel cells, and rechargeable metal-air batteries. The synthesis of stable, efficient, non-noble metal-based electrocatalysts for OER has been a long-standing challenge. In this work, a facile and scalable method to synthesize hollow and conductive iron-cobalt phosphide (Fe-Co-P) alloy nanostructures using an Fe-Co metal organic complex as a precursor is described. The Fe-Co-P alloy exhibits excellent OER activity with a specific current density of 10 mA/cm being achieved at an overpotential as low as 252 mV. The current density at 1.5 V (vs reversible hydrogen electrode) of the Fe-Co-P catalyst is 30.7 mA/cm, which is more than 3 orders of magnitude greater than that obtained with state-of-the-art Fe-Co oxide catalysts. Our mechanistic experiments and theoretical analysis suggest that the electrochemical-induced high-valent iron stabilizes the cobalt in a low-valent state, leading to the simultaneous enhancement of activity and stability of the OER catalyst.