The thermodynamic properties of magnesium hydride nanoparticles have been investigated by hydrogen decomposition pressure measurements using the Sieverts technique. A mechanochemical method was used to synthesize MgH(2) nanoparticles (down to approximately 7 nm in size) embedded in a LiCl salt matrix. In comparison to bulk MgH(2), the mechanochemically produced MgH(2) with the smallest particle size showed a small but measurable decrease in the decomposition reaction enthalpy (DeltaH decrease of 2.84 kJ/mol H(2) from DeltaH(bulk) = 74.06 +/- 0.42 kJ/mol H(2) to DeltaH(nano) = 71.22 +/- 0.49 kJ/mol H(2)). The reduction in DeltaH matches theoretical predictions and was also coupled with a similar reduction in reaction entropy (DeltaS decrease of 3.8 J/mol H(2)/K from DeltaS(bulk) = 133.4 +/- 0.7 J/mol H(2)/K to DeltaS(nano) = 129.6 +/- 0.8 J/mol H(2)/K). The thermodynamic changes in the MgH(2) nanoparticle system correspond to a drop in the 1 bar hydrogen equilibrium temperature (T(1 bar)) by approximately 6 degrees C to 276.2 +/- 2.4 degrees C in contrast to the bulk MgH(2) system at 281.8 +/- 2.2 degrees C. The reduction in the desorption temperature is less than that expected from theoretical studies due to the decrease in DeltaS that acts to partially counteract the effect from the change in DeltaH.

One of the limitations to the widespread use of hydrogen as an energy carrier is its storage in a safe and compact form. Herein, recent developments in effective high-capacity hydrogen storage materials are reviewed, with a special emphasis on light compounds, including those based on organic porous structures, boron, nitrogen, and aluminum. These elements and their related compounds hold the promise of high, reversible, and practical hydrogen storage capacity for mobile applications, including vehicles and portable power equipment, but also for the large scale and distributed storage of energy for stationary applications. Current understanding of the fundamental principles that govern the interaction of hydrogen with these light compounds is summarized, as well as basic strategies to meet practical targets of hydrogen uptake and release. The limitation of these strategies and current understanding is also discussed and new directions proposed.

No abstract

A series of monometallic borohydrides and borohydride eutectic mixtures have been investigated during thermal ramping by mass spectroscopy, differential scanning calorimetry, and photography. Mixtures of LiBH4-NaBH4, LiBH4-KBH4, LiBH4-Mg(BH4)2, LiBH4-Ca(BH4)2, LiBH4-Mn(BH4)2, NaBH4-KBH4, and LiBH4-NaBH4-KBH4 all displayed melting behaviour below that of the monometallic phases (up to 167 °C lower). Generally, each system behaves differently with respect to their physical behaviour upon melting. The molten phases can exhibit colour changes, bubbling and in some cases frothing, or even liquid-solid phase transitions during hydrogen release. Remarkably, the eutectic melt can also allow for hydrogen release at temperatures lower than that of the individual components. Some systems display decomposition of the borohydride in the solid-state before melting and certain hydrogen release events have also been linked to the adverse reaction of samples with impurities, usually within the starting reagents, and these may also be coupled with bubbling or frothing of the ionic melt.