The fuel cladding is one of the most important structural components for maintaining the integrity of a fuel channel and for safely exploitation of a nuclear power plant. The corrosion behavior of a fuel cladding material, Zy-4, under high pressure and temperatures conditions, was analyzed in a static isothermal autoclave under simulated primary water conditions—a LiOH solution at 310 °C and 10 MPa for up to 3024 h. After this, the oxides grown on the Zy-4 sample surface were characterized using electrochemical measurements, gravimetric analysis, metallographic analysis, SEM and XPS. The maximum oxide thicknesses evaluated by gravimetric and SEM measurements were in good agreement; both values were around 1.2 µm. The optical light microscopy (OLM) investigations identified the presence of small hydrides uniformly distributed horizontally across the alloy. EIS impedance spectra showed an increase in the oxide impedance for the samples oxidized for a long time. EIS plots has the best fit with an equivalent circuit which illustrated an oxide model that has two oxide layers: an inner oxide layer and outer layer. The EIS results showed that the inner layer was a barrier layer, and the outer layer was a porous layer. Potentiodynamic polarization results demonstrated superior corrosion resistance of the samples tested for longer periods of time. By XPS measurements we identified all five oxidation states of zirconium: Zr0 located at 178.5 eV; Zr4+ at 182.8 eV; and the three suboxides, Zr+, Zr2+ and Zr3+ at 179.7, 180.8 and 181.8 eV, respectively. The determination of Vickers microhardness completed the investigation.
The manuscript is focused on corrosion behavior of a Cr coating under CANada Deuterium Uranium(CANDU) primary circuit conditions. The Cr coating is obtained via the thermionic vacuum arc procedure on Zircaloy -4 cladding. The surface coating characterization was performed using metallographic analysis and scanning electron microscopy (SEM) with an energy dispersive spectra detector (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) investigations. The thickness of the Cr coating determined from SEM images is around 500 nm layers After the autoclaving period, the thickness of the samples increased in time slowly. The kinetic of oxidation established a logarithmic oxidation law. The corrosion tests for various autoclaving periods of time include electrochemical impedance spectroscopy (EIS) and potentiodynamic tests, permitting computing porosity and efficiency of protection. All surface investigations sustain electrochemical results and promote the Cr coating on Zircaloy-4 alloy autoclaved for 3024 h as the best corrosion resistance based on decrease in corrosion current density values simultaneously with the increase of the time spent in autoclave. A slow increase of Vickers micro hardness was observed as a function of the autoclaved period as well. The value reached for 3024 h being 219 Kgf/mm2 compared with 210 Kgf/mm2 value before autoclaving.
The present paper is a narrative review focused on a few important aspects and moments of trends surrounding materials and methods in sustainable nuclear energy, as an expression of applied chemistry support for more efficiency and safety. In such context, the paper is focused firstly on increasing alloy performance by modifying compositions, and elaborating and testing novel coatings on Zr alloys and stainless steel. For future generation reactor systems, the paper proposes high entropy alloys presenting their composition selection and irradiation damage. Nowadays, when great uncertainties and complex social, environmental, and political factors influence energy type selection, any challenge in this field is based on the concept of increased security and materials performance leading to more investigations into applied science.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.