The electrocatalytic activities of a wide range of ordered intermetallic phases toward a variety of potential fuels have been studied, and results have been compared to those of a pure polycrystalline platinum (Pt(pc)) electrode. A significant number of the ordered intermetallic phases exhibited enhanced electrocatalytic activity when compared to that of Pt, in terms of both oxidation onset potential and current density. The PtBi, PtIn, and PtPb ordered intermetallic phases appeared to be the most promising electrocatalysts tested thus far for fuel cell applications. PtPb, in particular, showed an onset potential that was 100 mV less positive and a peak current density approximately 40 times higher than those observed for Pt in the case of methanol oxidation. The ability to control the geometric and electronic structures of the electrocatalytic material by using ordered intermetallic phases has been shown to be a promising direction of inquiry in the search for superior electrocatalysts for fuel cell applications.

The oxidation pathways of methanol (MeOH) have been the subject of intense research due to its possible application as a liquid fuel in polyelectrolyte membrane (PEM) fuel cells. The design of improved catalysts for MeOH oxidation requires a deep understanding of these complex oxidation pathways. This paper will provide a discussion of the literature concerning the extensive research carried out in acidic and alkaline electrolytes. It will highlight techniques that have proven useful in the determination of product ratios, analysis of surface poisoning, anion adsorption, and oxide formation processes, in addition to the effects of temperature on the MeOH oxidation pathways at bulk polycrystalline platinum (Pt(poly)) electrodes. This discussion will provide a framework with which to begin the analysis of activation energy (E(a)) values. This kinetic parameter may prove useful in characterizing the rate-limiting step of the MeOH oxidation at an electrode surface. This paper will present a procedure for the determination of E(a) values for MeOH oxidation at a Pt(poly) electrode in acidic and alkaline media. Values from 24-76 kJ mol(-1) in acidic media and from 36-86 kJ mol(-1) in alkaline media were calculated and found to be a function of applied potential and direction of the potential sweep in a voltammetric experiment. Factors that influence the magnitude of the calculated E(a) include surface poisoning from MeOH oxidation intermediates, anion adsorption from the electrolyte, pH effects, and oxide formation processes. These factors are all potential, and temperature, dependent and must clearly be addressed when citing E(a) values in the literature. Comparison of E(a) values must be between systems of comparable electrochemical environment and at the same potential. E(a) values obtained on bulk Pt(poly), compared with other catalysts, may give insight into the superiority of other Pt-based catalysts for MeOH oxidation and lead to the development of new catalysts which lower the E(a) barrier at a given potential, thus driving MeOH oxidation to completion.

A dual electrolyte H2/O2 fuel cell system employing a planar microfluidic membraneless fuel cell has been investigated and compared to single electrolyte H2/O2 systems under analogous conditions. The fuel is H2 dissolved in 0.1 M KOH (pH 13), and the oxidant is O2 dissolved in 0.1 M H2SO4 (pH 0.9), comprising a system with a calculated thermodynamic potential of 1.943 V (when 1 M H2 and O2 concentrations are assumed). This value is well above the calculated thermodynamic maximum of 1.229 V for an acid, or alkaline, single electrolyte H2/O2 fuel cell. Experimentally, open-circuit potentials in excess of 1.4 V have been achieved with the dual electrolyte system. This is a 500 mV increase in the open circuit potentials observed for single electrolyte H2/O2 systems also studied. The dual electrolyte fuel cell system shows power generation of 0.6 mW/cm2 from a single device, which is nearly 0.25 mW/cm2)greater than the values obtained for single electrolyte H2/O2 fuel cell systems studied. Microchannels of varying dimensions have been employed to study both the single and dual electrolyte H2/O2 systems. Channel thickness variation and the flow rate dependences of power generation are also addressed.

Ordered intermetallic phases of PtBi and PtPb have been prepared and studied ͓using cyclic voltammetry, rotating disk electrode voltammetry, and Fourier transform infrared ͑FTIR͔͒ as potential fuel cell electrocatalysts using formic acid as a model system, elucidating electrochemical activity, reaction kinetics, and resistance to CO surface poisoning. Both electrodes displayed activity superior to that of pure Pt under any conditions tested but were found to roughen at significantly positive potentials ͑typically above ϩ400 mV vs. Ag/AgCl͒ in acidic media, likely due to preferential dissolution of the p-block metal ͑Bi, Pb͒. Each electrode was subjected to a variety of surface treatments to obtain suitable cleaning methods. Mechanical polishing with alumina was found to be the best treatment for PtBi, while PtPb was fairly insensitive to treatment procedures and parameters. Using the rotating disk electrode method, a value of 1.4 ϫ 10 Ϫ4 cm s Ϫ1 was obtained for the heterogeneous charge-transfer rate constant for PtPb in formic acid. Both PtBi and PtPb exhibited high tolerance to CO poisoning; no evidence of CO adsorption at any potential was found via FTIR.