Here, we demonstrate that light and oxygen-induced degradation is the main reason for the low operational stability of methylammonium lead triiodide (MeNH3PbI3) perovskite solar cells exposed to ambient conditions.

Ion migration has been proposed as a possible cause of photovoltaic current–voltage hysteresis in hybrid perovskite solar cells. A major objection to this hypothesis is that hysteresis can be reduced by changing the interfacial contact materials; however, this is unlikely to significantly influence the behaviour of mobile ionic charge within the perovskite phase. Here, we show that the primary effects of ion migration can be observed regardless of whether the contacts were changed to give devices with or without significant hysteresis. Transient optoelectronic measurements combined with device simulations indicate that electric-field screening, consistent with ion migration, is similar in both high and low hysteresis CH3NH3PbI3 cells. Simulation of the photovoltage and photocurrent transients shows that hysteresis requires the combination of both mobile ionic charge and recombination near the perovskite-contact interfaces. Passivating contact recombination results in higher photogenerated charge concentrations at forward bias which screen the ionic charge, reducing hysteresis.

The maximum open-circuit voltage of a solar cell can be evaluated in terms of its ability to emit light. We herein verify the reciprocity relation between the electroluminescence spectrum and subband-gap quantum efficiency spectrum for several photovoltaic technologies at different stages of commercial development, including inorganic, organic, and a type of methyl-ammonium lead-halide CH 3 NH 3 PbI 3−x Cl x perovskite solar cells. Based on the detailed balance theory and reciprocity relations between light emission and light absorption, voltage losses at open circuit are quantified and assigned to specific mechanisms, namely, absorption edge broadening and nonradiative recombination. The voltage loss due to nonradiative recombination is low for inorganic solar cells (0.04-0.21 V), while for organic solar cell devices it is larger but surprisingly uniform, with values of 0.34-0.44 V for a range of material combinations. We show that, in CH 3 NH 3 PbI 3−x Cl x perovskite solar cells that exhibit hysteresis, the loss to nonradiative recombination varies substantially with voltage scan conditions. We then show that for different solar cell technologies there is a roughly linear relation between the power conversion efficiency and the voltage loss due to nonradiative recombination.