Three-dimensional printed surgical guides increase the precision of orthodontic mini-implant placement. The purpose of this research was to investigate the effects of disinfection and of two types of autoclave sterilization on the mechanical properties of 3D printed surgical guides obtained via the SLA (stereolithography) and DLP (digital light processing) printing methods. A total of 96 standard specimens (48 SLA and 48 DLP) were printed to analyze the tensile and flexural properties of the materials. A total of 80 surgical guide (40 SLA and 40 DLP) specimens from each printing method were classified into four groups: CG (control group); G1, disinfected with 4% Gigasept (Gigasept Instru AF; Schülke & Mayer Gmbh, Norderstedt, Germany); G2, autoclave-sterilized (121 °C); and G3, autoclave-sterilized (134 °C). Significant differences in the maximum compressive load were determined between the groups comprising the DLP-(p < 0.001) and the SLA- (p < 0.001) printed surgical guides. Groups G2 (p = 0.001) and G3 (p = 0.029) showed significant parameter modifications compared with the CG. Disinfection with 4% Gigasept (Gigasept Instru AF; Schülke & Mayer Gmbh, Norderstedt, Germany) is suitable both for SLA- and DLP-printed surgical guides. Heat sterilization at both 121 °C and 134 °C modified the mechanical properties of the surgical guides.
Pre-impregnated E-glass fibre nets and polymer pre-impregnated E-glass unidirectional fibres are useful in reinforcing acrylic resin complete dentures especially were heavy occlusal forces are involved. Glass fibre reinforcement will be applied on the tension side in both cases (total fibre reinforcement and partial fibre reinforcement). The reinforcement cannot replace the necessary linings and occlusal adjustments.
This 2-year study illustrated that short implants are a viable option in selected clinical scenarios. Short implants with wider diameters are preferred because they have less marginal implant bone loss.
The purpose of this study was to evaluate the clinical outcome of feldspathic ceramic laminate veneers over a 7-year period using minimally invasive techniques, such as vertical preparation (without prosthetic finish line), or no preparation (no-prep). A total of 170 feldspathic ceramic veneers were cemented in the anterior region, including 70 maxillary and 100 mandibular veneers, after special conditioning of the teeth and restorations. The veneers were evaluated using the FDI World Dental Federation criteria evaluation kit after recalling all the patients between February and June 2021. In total, 14 feldspathic veneers failed and were replaced with lithium disilicate because of core fracture, and 10 cases of chipping occurred on the ceramic surface and were polished. The overall survival rate was 91.77% for up to 7 years of function, with a failure rate of 8.23%. In this retrospective survival analysis, the failures, including the fracture of veneers and dental hard tissue, occurred both in prep and no-prep teeth. No failures were observed in veneers with a maximum thickness of 0.5 mm compared to those with a maximum thickness of 1 mm, 1.5 mm, 2 mm, and 2.5 mm.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.