Thiol monolayer-protected Au clusters (MPCs) were prepared using dendrimer templates, deposited onto a high-surface-area titania, and then the thiol stabilizers were removed under H2/N2. The resulting Au catalysts were characterized with transmission electron microscopy, X-ray photoelectron spectroscopy, and infrared spectroscopy of adsorbed CO. The Au catalysts prepared via this route displayed minimal particle agglomeration during the deposition and activation steps. Structural data obtained from the physical characterization of the Au catalysts were comparable to features exhibited from a traditionally prepared standard Au catalyst obtained from the World Gold Council (WGC). A differential kinetic study of CO oxidation catalysis by the MPC-prepared Au and the standard WGC catalyst showed that these two catalyst systems have essentially the same reaction order and Arrhenius apparent activation energies (28 kJ/mol). However, the MPC-prepared Au catalyst shows 50% greater activity for CO oxidation. Using a Michaelis−Menten approach, the oxygen binding constants for the two catalyst systems were determined and found to be essentially the same within experimental error. To our knowledge, this kinetic evaluation is the first experimental determination of oxygen binding by supported Au nanoparticle catalysts under working conditions. The values for the oxygen binding equilibrium constant obtained from the Michaelis−Menten treatment (ca. 29−39) are consistent with ultra-high-vacuum measurements on model catalyst systems and support density functional theory calculations for oxygen binding at corner or edge atoms on Au nanoparticles and clusters.

New bimetallic Ni-Au supported nanoparticle catalysts were prepared by using dendrimer templated nanoparticles. Amine-terminated generation 5 polyamidoamine (PAMAM) dendrimers were anchored to a commercial silica with a siloxane linked anhydride. The dendrimer was then alkylated and used to template Ni-Au nanoparticles, which were subsequently extracted into organic solution as thiol monolayer protected clusters (MPCs). Transmission electron microscopy (TEM) and energy dispersive spectroscopy (EDS) indicated bimetallic nanoparticles of about 2 nm in size. Nanoparticles were deposited onto P-25 TiO 2 , and the capping thiol ligands were removed under flowing H 2 . DRIFTS infrared spectra of adsorbed CO showed only Au on the catalyst surface; no bands attributable to Ni or NiO were observed. Density functional theory (DFT) calculations showed that Au is substantially more stable than Ni on the surface of model slabs. DFT calculations also indicated that the incorporation of Ni into Au slabs results in stronger adsorption of O and CO on Au surfaces. Catalysts were evaluated with low-temperature CO oxidation. Kinetics studies indicated a substantial modification of Au catalysis through Ni incorporation. Apparent activation energies decreased by more than 50% and O 2 reaction orders increased from 0.2 to 0.9. These results are placed in the context of the available literature regarding support effects for Au catalysts. The observed changes to Au chemistry in the current work are substantially larger than previous reports have attributed to support effects. A Michaelis-Menten (enzyme) treatment of the kinetics data indicated that the O 2 reactivity constant increased by a factor of 40 for catalysts with high Ni content. This was in good qualitative agreement with the DFT calculations. At the same time, the introduction of Ni reduced the relative number of catalytically active sites.