Iron oxide colloidal nanomagnets generate heat when subjected to an alternating magnetic field. Their heating power, governed by the mechanisms of magnetic energy dissipation for single-domain particles (Brown and Néel relaxations), is highly sensitive to the crystal size, the material, and the solvent properties. This study was designed to distinguish between the contributions of Néel and Brownian mechanisms to heat generation. Anionic nanocrystals of maghemite and cobalt ferrite, differing by their magnetic anisotropy, were chemically synthesized and dispersed in an aqueous suspension by electrostatic stabilization. The particles were size-sorted by successive electrostatic phase separation steps. Parameters governing the efficiency of nanomagnets as heat mediators were varied independently; these comprised the particle size (from 5 to 16.5 nm), the solvent viscosity, magnetic anisotropy, and the magnetic field frequency and amplitude. The measured specific loss powers (SLPs) were in quantitative agreement with the results of a predictive model taking into account both Néel and Brown loss processes and the whole particle size distribution. By varying the carrier fluid viscosity, we found that Brownian friction within the carrier fluid was the main contributor to the heating power of cobalt ferrite particles. In contrast, Néel internal rotation of the magnetic moment accounted for most of the loss power of maghemite particles. Specific loss powers were varied by 3 orders of magnitude with increasing maghemite crystal size (from 4 to 1650 W/g at 700 kHz and 24.8 kA/m). This comprehensive parametric study provides the groundwork for the use of anionic colloidal nanocrystals to generate magnetically induced hyperthermia in various media, including complex systems and biological materials.

Iron oxide nanocrystals (IONCs) are appealing heat mediator nanoprobes in magnetic-mediated hyperthermia for cancer treatment. Here, specific absorption rate (SAR) values are reported for cube-shaped water-soluble IONCs prepared by a one-pot synthesis approach in a size range between 13 and 40 nm. The SAR values were determined as a function of frequency and magnetic field applied, also spanning technical conditions which are considered biomedically safe for patients. Among the different sizes tested, IONCs with an average diameter of 19 ± 3 nm had significant SAR values in clinical conditions and reached SAR values up to 2452 W/g(Fe) at 520 kHz and 29 kAm(-1), which is one of the highest values so far reported for IONCs. In vitro trials carried out on KB cancer cells treated with IONCs of 19 nm have shown efficient hyperthermia performance, with cell mortality of about 50% recorded when an equilibrium temperature of 43 °C was reached after 1 h of treatment.