A novel chitosan-based biopolymer dye possessing antibacterial properties was synthesized by reaction of O-carboxymethyl chitosan and Acid Red GR. The synthesized materials were characterized by Fourier transform infrared spectroscopy (FTIR), degree of substitution (DS), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TG), X-ray diffraction (XRD), water solubility test, antibacterial property test, and dyeing performance, including dye uptake, color difference, and fastness. Results showed that the synthesized dye was combined by -NH 3 + of O-carboxymethyl chitosan and the sulfonic group of Acid Red GR. According to the comprehensive analysis of XRD and water solubility, the introduction of the carboxymethyl group and acid dye molecule changed the structure of the chitosan from compact to loose, which improved the synthesized dye's water solubility. However, the thermal stability of the synthesized dye was decreased. The antibacterial property of the poplar wood dyed with the synthesized dye was enhanced and its antibacterial rate, specifically against Staphylococcus aureus and Escherichia coli, also increased to a rate of more than 99%. However, the dye uptake of the synthesized dye was lower than that of the original dye. Despite this, though, the dyeing effect of the synthesized dye demonstrated better water-fastness, and light-fastness than the original dye. Therefore, the novel chitosan-based biopolymer dye can be a promising product for wood dyeing.
This study was to explore the conversion of low-cost bio-residuals into high value-added cellulose nanocrystals. Two enzymatic hydrolyzed residuals (i.e., HRMMW and HRSPW) were collected from two different bio-ethanol producing processes—hydrolyzing medium-milled wood (MMW) and hydrolyzing acid sulfite pretreated wood (SPW), respectively. The results showed that both residuals contained over 20 wt % glucan with a crystallinity of about 30%, confirming the existence of cellulose in a well-organized structure in two bio-residuals. The cellulose nanocrystals (CNCs) were successfully extracted by first bleaching the hydrolyzed residuals to remove lignin and then hydrolyzing them with sulfuric acid. The resulting CNCs displayed the flow birefringence under two crossed polarizers. Compared with CNCs from microfibrillated cellulose (CNCMCC), HRMMW and its resulted CNC present the smallest particle size and aspect ratio. CNCMCC had the larger particle size, aspect ratio, and higher z-potential value, CNCSPW presented a similar morphology to CNCMCC, and had the largest aspect ratio. The CNCMCC enhanced its high crystallinity to 85.5%. However, CNCMMW and CNCSPW had a better thermal stability and higher activation energy as well as onset temperature and maximum decomposition temperature. As a result, the CNCs from bio-ethanol residuals are valued and promising cellulose nanoparticle resources.
This study was to develop novel soy protein isolate-based films for packaging using halloysite nanotubes (HNTs), poly-vinyl alcohol (PVA), and 1,2,3-propanetriol-diglycidyl-ether (PTGE). The structural, crystallinity, opacity, micromorphology, and thermal stability of the resultant SPI/HNTs/PVA/PTGE film were analyzed by the Attenuated total reflectance-Fourier transformed infrared (ATR-FTIR) spectroscopy, X-ray diffraction (XRD), UV-Vis spectrophotometry, scanning electron microscopy (SEM), and thermo-gravimetric analysis (TGA). The SPI/HNTs/PVA/PTGE film illustrated that HNTs were uniformly dispersed in the SPI matrix and the thermal stability of the film was enhanced. Furthermore, the tensile strength (TS) of the SPI/HNTs/PVA/PTGE film was increased by 329.3% and the elongation at the break (EB) remained unchanged. The water absorption (WA) and the moisture content (MC) were decreased by 5.1% and 10.4%, respectively, compared to the unmodified film. The results highlighted the synergistic effects of SPI, HNTs, PVA, and PTGE on the mechanical properties, water resistance, and thermal stability of SPI films, which showed excellent strength and flexibility. In short, SPI films prepared from HNTs, PVA, and PTGE showed considerable potential as packaging materials.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.