The structural properties of coevaporated thin films of pentacene (PEN) and perfluoropentacene (PFP) on SiO(2) were studied using x-ray reflectivity and grazing incidence x-ray diffraction. Reciprocal space maps of the coevaporated thin films with different volume fractions reveal the coexistence of two different molecular mixed PEN-PFP phases together with the pure PEN and PFP crystallites. The crystal structure of PEN:PFP blends does not change continuously with volume fraction, instead the proportion of the appropriate phases changes, as seen from the diffraction analysis. Additional temperature dependent experiments reveal that the fraction of the two mixed PEN-PFP phases varies with growth temperature. The λ-phase (molecular plane parallel to the substrate) is metastable and induced by low growth temperature. The σ-phase (molecular plane nearly perpendicular to the substrate) is thermally stable and nucleates predominantly at high growth temperatures.
Charge transport in organic thin film transistors takes place in the first few molecular layers in contact with the gate dielectric. Here we demonstrate that the charge transport pathways in these devices are extremely sensitive to the orientational defects of the first monolayers, which arise from specific growth conditions. Although these defects partially heal during the growth, they cause depletion of charge carriers in the first monolayer, and drive the current to flow in the monolayers above the first one. Moreover, the residual defects induce lower crystalline order and charge mobility. These results, which are not intuitively explained by electrostatics arguments, have been obtained by combining in situ real time structural and electrical characterization together with ex situ AFM measurements, on thin films of a relevant n-type organic semiconductor, N,N'-bis(n-octyl)-dicyanoperylene-3,4:9,10-bis dicarboximide grown by sublimation in a quasi-layer-by-layer mode at different substrate temperatures.
To achieve organic solar cells with a broadened spectral absorption, we aim to promote the growth of the near-infrared (NIR)-active polymorph of lead phthalocyanine (PbPc) on a relevant electrode for solar cell applications. We studied the effect of different substrate modification layers on PbPc thin film structure as a function of thickness and deposition rate (rdep). We characterized crystallinity and orientation by grazing incidence X-ray diffraction (GIXD) and in situ X-ray reflectivity (XRR) and correlated these data to the performance of bilayer solar cells. When deposited onto a self-assembled monolayer (SAM) or a molybdenum oxide (MoO3) buffer layer, the crystallinity of the PbPc films improves with thickness. The transition from a partially crystalline layer close to the substrate to a more crystalline film with a higher content of the NIR-active phase is enhanced at low rdep, thereby leading to solar cells that exhibit a higher maximum in short circuit current density (JSC) for thinner donor layers. The insertion of a CuI layer induces the formation of strongly textured, crystalline PbPc layers with a vertically homogeneous structure. Solar cells based on these templated donor layers show a variation of JSC with thickness that is independent of rdep. Consequently, without decreasing rdep we could achieve JSC=10 mA/cm2, yielding a bilayer solar cell with a peak external quantum efficiency (EQE) of 35% at 900 nm, and an overall power conversion efficiency (PCE) of 2.9%.
In ternary water-oil-nonionic alkyl polyglycol ether (CiEj) microemulsions, an increase in efficiency is always accompanied by the formation of a lamellar (LR) phase. The addition of an amphiphilic block copolymer to the ternary base system increases the efficiency of the microemulsion drastically while suppressingsat least partlysthe formation of the L R phase. However, amphiphilic block copolymers can be used not only to suppress the formation of lyotropic liquid crystals but also for the opposite effect, namely, to induce their formation. To understand to what extent the increase in efficiency is accompanied by the formation of lyotropic liquid crystals, we studied phase diagrams of water-n-alkane-n-alkyl polyglycol ethers (C iEj)-PEPX-PEOY at a constant volume fraction of oil in the water/oil mixture. Using polymers of the poly(ethylene propylene)-copoly(ethylene oxide) type, with MPEP ) X kg mol -1 and MPEO ) Y kg mol -1 , we determined phase diagrams as a function of the polymer concentration, size, and symmetry. Moreover, the influence of a particular polymer mixture was studied, which turned out to be the best system if both a high efficiency and a low tendency to form an L R phase are needed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.