The shape of gold nanoparticles has been successfully tuned among penta-twinned decahedrons, truncated tetrahedrons, cubes, octahedrons, hexagonal thin plates by introducing a small amount of salt into a N,N-dimethylformamide (DMF) solution containing poly(vinyl pyrrolidone) (PVP), and changing the temperature or the concentration of the gold precursor.
Single-crystal PbS nanorods were successfully synthesized through a simple hydrothermal route using PEO-PPO-PEO triblock copolymer (P123) as a structure-directing agent. The XRD pattern indicates that the crystal structure of the nanorods is face-centre-cubic rocksalt. A SEM image shows that the nanorods have a diameter of 40-70 nm and a length of 200-600 nm, and both tips exhibit taper-like structures. HRTEM and SAED images reveal the single-crystalline nature of the nanorods with the growth along the (111) direction. The experimental results indicated that the P123 concentration and reaction temperature played important roles in controlling the morphology of the PbS nanostructures. The optical property of PbS nanorods was investigated by UV-Vis absorption spectroscopy and the band structure was calculated by the B3LYP hybrid density functional theory.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.