A sol-gel methodology has been duly developed in order to perform a controlled covalent coupling of tetrapyrrole macrocycles (e.g., porphyrins, phthalocyanines, naphthalocyanines, chlorophyll, etc.) to the pores of metal oxide networks. The resulting absorption and emission spectra intensities in the UV-VIS-NIR range have been found to depend on the polarity existing inside the pores of the network; in turn, this polarization can be tuned through the attachment of organic substituents to the tetrapyrrrole macrocycles before bonding them to the pore network. The paper shows clear evidence of the real possibility of maximizing fluorescence emissions from metal-free bases of substituted tetraphenylporphyrins, especially when these molecules are bonded to the walls of functionalized silica surfaces via the attachment of alkyl or aryl groups arising from the addition of organo-modified alkoxides.
Polymeric fibers have been used since the 1980s for improvement of the concrete. However, high mechanical performance has been obtained at high cost and using complex technologies. At least two parameters are important here: dimensions and surface characteristics of the fibers. We have modified nylon 6,12 fiber surfaces by 5, 10, 50, and 100 kGy gamma irradiation dosages. Tensile strength of the irradiated fibers was determined and then the fibers mixed at 1.5%, 2.0%, and 2.5% in volume with Portland cement, gravel, sand, and water. The compressive strength of the fiber reinforced concrete (FRC) was evaluated and the results were compared with results for similar materials reported before. The highest values of the compressive strength of FRC are seen for fibers at 50 kGy and 2.0% in volume of fiber; the strength is 122.2 MPa, as compared to 35 MPa for simple concrete without fibers. We advance a mechanism by which the fiber structure can be affected by gamma irradiation resulting in the compressive strength improvement of the concrete.
The synthetic tetrapyrrole macrocycles, such as porphyrins (H2P) and phthalocyanines (H2Pc), exhibit interesting physicochemical properties suitable to be used in modern technology. For many applications, those species should be trapped or fixed inside graphite, hydrotalcites, silica, TiO2, or polymers. Methodologies for the optimization of the properties of porphyrins, trapped or fixed inside polymers, have been barely developed. Our research works in the development of methodologies for the optimization of incorporation and display of properties of tetrapyrrole macrocycles inside inorganic, polymeric, or hybrid networks. This paper shows some results about the effect of the spatial disposition of the amine (–NH2) groups attached on the periphery of substituted tetraphenylporphyrins, on the Nylon 66 structure and on the display of the physicochemical properties of the trapped macrocycles. Nylon 66 was synthesized from adipoyl chloride and hexamethylenediamine in presence of tetraphenylporphyrins substituted with –NH2groups localized at theortho- orpara-positions of the phenyls. Cobalt complexes formation was used to quantify the amount of porphyrins in the polymer fibers. Characterization results show that the spatial position of amine groups of the porphyrins has important structural and textural effect on the Nylon 66 fibers and on the fluorescence of the porphyrins integrated into the fibers.
Fiber reinforced concrete (FRC) contains fibers physically mixed with gravel, sand, cement, and water. So far, adequate mechanical performance of FRC has been obtained at high cost and using complex technologies; important here is the geometry and surface characteristics of the polymers. We have modified polymeric‐fiber surfaces by using gamma radiation. Irradiated polypropylene (PP) fibers were submitted to 0, 5, 10, 50, and 100 kGy of gamma irradiation dosages. First, tensile strength of PP fibers was evaluated, and then fibers blended at 0, 1.0, 1.5, and 2.0% in volume with Portland cement, gravel, sand, and water. The highest values of compressive strength were obtained with irradiated‐fibers at 10 kGy and 1.5% in volume of fiber. The result is 101 MPa, as compared to 35 MPa for simple concrete without fibers. POLYM. ENG. SCI., 45:1426–1431, 2005. © 2005 Society of Plastics Engineers
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.