The structure and chemical composition of the shell distribution on NaYF 4 /NaGdF 4 core/shell nanocrystals have been investigated with scanning transmission electron microscopy (STEM), electron energy loss spectroscopy (EELS), and energy-dispersive X-ray spectroscopy (EDS). The core and shell contrast in the high-angle annular dark-field (HAADF) images combined with the EELS and EDS signals indicate that Gd is indeed on the surface, but for many of the particles, the shell growth was anisotropic.
SECTION Nanoparticles and Nanostructures
Highly {100} oriented Pt deposits were prepared by electrodeposition from a 10 mM HCl, 100 mM KCl and Na 2 PtCl 6 .xH 2 O electrolyte. The deposits were prepared in the form of thin fi lms and array of nanowires. A qualitative assessment of the proportion of {100} oriented Pt surfaces was obtained through X-ray diffraction measurements and cyclic voltammetry in 0.5 M H 2 SO 4 . The effect of the deposition potential, E dep , temperature of the electrolyte, T dep , platinum salt concentration [Na 2 PtCl 6 .xH 2 O], and nature of the substrate were investigated. It was shown that the proportion of {100} oriented Pt surfaces reaches a maximum for E dep = −0.35 V vs SCE. Moreover, this proportion increases steadily as T dep and [Na 2 PtCl 6 .xH 2 O] are decreased from 75 to 25 ° C and from 2.5 to 0.25 mM, respectively. Scanning electron microscopy and high-resolution transmission electron microscopy micrographs indicate that the more oriented samples are made of pine tree-like structures that are effectively single crystals, and that the growth facets appear to be close to the {001} plane. This observation also clearly indicates that the plane exposed during the CV experiment is also {001}. As suggested by these micrographs, the fi lms and nanowires are highly porous and roughness factors as large as 1000 were obtained on highly {100} oriented Pt nanowires. The predominance of {100} facets is attributed to their energetically favoured growth in the presence of hydrogen, and is shown to be signifi cantly enhanced when the mass transport of Pt 4 + is limited. Due to the predominance of {100} facets, the normalized electrocatalytic activity ( μ A cm − 2 Pt ) for the electro-oxidation of hydrazine and ammonia is higher than non-oriented polycrystalline Pt by a factor of 4 and 2.7, respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.