No abstract

Gold nanoparticle (Au NP) mirrors, which exhibit both high reflectance and electrical conductance, were self-assembled at a [heptane + 1,2-dichloroethane]/water liquid/liquid interface. The highest reflectance, as observed experimentally and confirmed by finite difference time domain calculations, occurred for Au NP films consisting of 60 nm diameter NPs and approximate monolayer surface coverage. Scanning electrochemical microscopy approach curves over the interfacial metallic NP films revealed a transition from an insulating to a conducting electrical material on reaching a surface coverage at least equivalent to the formation of a single monolayer. Reflectance and conductance transitions were interpreted as critical junctures corresponding to a surface coverage that exceeded the percolation threshold of the Au NP films at the [heptane + 1,2-dichloroethane]/water interface.

Polyelectrolyte/gold nanoparticle multilayers composed of poly(L-lysine) (pLys) and mercaptosuccinic acid (MSA) stabilized gold nanoparticles (Au NPs) were built up using the electrostatic layer-by-layer self-assembly technique upon a gold electrode modified with a first layer of MSA. The assemblies were characterized using UV-vis absorption spectroscopy, cyclic and square-wave voltammetry, electrochemical impedance spectroscopy, and atomic force microscopy. Charge transport through the multilayer was studied experimentally as well as theoretically by using two different redox pairs [Fe(CN) 6 ] 3-/4-and [Ru(NH 3 ) 6 ] 3+/2+ . This paper reports a large sensitivity to the charge of the outermost layer for the permeability of these assemblies to the probe ions. With the former redox pair, dramatic changes in the impedance response were obtained for thin multilayers each time a new layer was deposited. In the latter case, the multilayer behaves as a conductor exhibiting a strikingly lower impedance response, the electric current being enhanced as more layers are added for Au NP terminated multilayers. These results are interpreted quite satisfactorily by means of a capillary membrane model that encompasses the wide variety of behaviors observed. It is concluded that nonlinear slow diffusion through defects (pinholes) in the multilayer is the governing mechanism for the [Fe(CN) 6 ] 3-/4-species, whereas electron transfer through the Au NPs is the dominant mechanism in the case of the [Ru(NH 3 ) 6 ] 3+/2+ pair.

Electrochemical impedance spectroscopy, Fourier transform infrared reflection-absorption spectroscopy, and cyclic voltammetry were employed to characterize polyelectrolyte multilayers (PEMs) fabricated with poly-(styrenesulfonate) as the polyanion and the polypeptides poly-L-histidine, poly-L-lysine, and poly-L-arginine as polycations. The layer-by-layer electrostatic assembly was produced onto alkanethiol-modified gold surfaces. The frequency response reveals that the effect of the number of layers seems to be related to a progressive reduction in the active area of the PEM-modified electrodes. The active area after the deposition of seven layers can be lower than 10% of its original value. The film surface is then inhomogeneous with respect to the transport of the electroactive species and has spots through which transport is quite favored. These structural features of the PEM have been taken into account in the theoretical model of ion transport and very good agreement with the experimental impedance results has been found.