BackgroundCyanoacrylate(CA)-based tissue adhesives, although not widely used, are a feasible option to fix a mesh during abdominal hernia repair, due to its fast action and great bond strength. Their main disadvantage, toxicity, can be mitigated by increasing the length of their alkyl chain. The objective was to assess the in vitro cytotoxicity and in vivo biocompatibility in hernia repair of CAs currently used in clinical practice (Glubran(n-butyl) and Ifabond(n-hexyl)) and a longer-chain CA (OCA(n-octyl)), that has never been used in the medical field.MethodsFormaldehyde release and cytotoxicity of unpolymerized(UCAs) and polymerized CAs(PCAs) were evaluated by macroscopic visual assessment, flow cytometry and Alamar Blue assays. In the preclinical evaluation, partial defects were created in the rabbit abdominal wall and repaired by fixing polypropylene prostheses using the CAs. At 14 days post-surgery, animals were euthanized for morphology, macrophage response and cell damage analyses.ResultsFormaldehyde release was lower as the molecular weight of the monomer increased. The longest side-chain CA(OCA) showed the highest cytotoxicity in the UCA condition. However, after polymerization, was the one that showed better behavior on most occasions. In vivo, all CAs promoted optimal mesh fixation without displacements or detachments. Seroma was evident with the use of Glubran, (four of six animals: 4/6) and Ifabond (2/6), but it was reduced with the use of OCA (1/6). Significantly greater macrophage responses were observed in groups where Glubran and Ifabond were used vs. sutures and OCA. TUNEL-positive cells were significantly higher in the Glubran and OCA groups vs. the suture group.ConclusionsAlthough mild formaldehyde release occurred, OCA was the most cytotoxic during polymerization but the least once cured. The CAs promoted proper mesh fixation and have potential to replace traditional suturing techniques in hernia repair; the CAs exhibited good tissue integration and effective short-term biocompatibility, with the slightest seroma and macrophage response induced by OCA.

Human Wharton's jelly stem cells (HWJSC) emerged as a potential source of viable cells for use in tissue engineering. In this work, we have analyzed the transdifferentiation capabilities of HWJSC towards transdifferentiated endothelial-like cells (Tr-ELC) in order to establish the potential usefulness of these cells in vascular tissue engineering. Our results show that Tr-ELC became more polygonal and less proliferative than HWJSC, resembling the structure and proliferation rate of the endothelial cells. In addition, the markers of mesenchymal undifferentiation CD9, E-cad, PODXL, and SSEA-4 are downregulated in Tr-ELC, suggesting that these cells can be in the process of adult differentiation. Besides, RT-PCR and microarray analyses revealed that some genes with a role in defining the endothelial phenotype and structure are upregulated (VEGF-R1, EDF1, AAMP, CD31, CD34, CDH5, and ICAM2) or downregulated (VEGF) in Tr-ELC, although a number of genes related to relevant endothelial cell functions (CD36, ECE2, VWF, THBD, PGI2, ECE1, and ACE) did not change or were only partially induced. All this implies that HWJSC are able to efficiently transdifferentiate towards Tr-ELC at the phenotypical level following a hierarchical pattern of gene activation, with an earlier induction of morphological and phenotypical genes.

In vitro and in vivo studies described the myokine IL-15 and its receptor IL-15Rα as anabolic/anti-atrophy agents, however, the protein expression of IL-15Rα has not been measured in human skeletal muscle and data regarding IL-15 expression remain inconclusive. The purpose of the study was to determine serum and skeletal muscle IL-15 and IL-15Rα responses to resistance exercise session and to analyze their association with myofibrillar protein synthesis (MPS). Fourteen participants performed a bilateral leg resistance exercise composed of four sets of leg press and four sets of knee extension at 75% 1RM to task failure. Muscle biopsies were obtained at rest, 0, 4 and 24 hours post-exercise and blood samples at rest, mid-exercise, 0, 0.3, 1, 2, 4 and 24 hours post-exercise. Serum IL-15 was increased by ~5.3-fold immediately post-exercise, while serum IL-15Rα decreased ~75% over 1 hour post-exercise (P<.001). Skeletal muscle IL-15Rα mRNA and protein expression were increased at 4 hours post-exercise by ~2-fold (P<.001) and ~1.3-fold above rest (P=.020), respectively. At 24 hours post-exercise, IL-15 (P=.003) and IL-15Rα mRNAs increased by ~2-fold (P=.002). Myofibrillar fractional synthetic rate between 0-4 hours was associated with IL-15Rα mRNA at rest (r=.662, P=.019), 4 hours (r=.612, P=.029), and 24 hours post-exercise (r=.627, P=.029). Finally, the muscle IL-15Rα protein up-regulation was related to Leg press 1RM (r=.688, P=.003) and total weight lifted (r=.628, P=.009). In conclusion, IL-15/IL-15Rα signaling pathway is activated in skeletal muscle in response to a session of resistance exercise.

The use of polymer coatings that slowly release non-antibiotic drugs seems to be a good strategy to prevent implant contamination and reduce the onset of resistant bacterial strains. Even though the prophylactic designs described in this review are mainly focused on hernia repair meshes, these strategies can be extrapolated to other implantable devices, regardless of their design, shape or dimension.

Human umbilical cord Wharton's jelly stem cells (HWJSCs) are gaining attention as a possible clinical source of mesenchymal stem cells for cell therapy and tissue engineering due to their high accessibility, expansion potential, and plasticity. We employed a combination of highly sensitive techniques to determine the average cell viability levels and proliferation capabilities of 10 consecutive cell passages of cultured HWJSCs and then used RNA microarrays to identify genes associated with changes in cell viability levels. We found an initial decrease in cell viability from the first to the third cell passage followed by an increase until the sixth passage and a final decrease from the sixth to tenth cell passages. The highest cell viability levels corresponded to the fifth and sixth passages. The intracellular ionic contents of potassium, sodium, and chlorine suggest that the lower cell viability levels at passages 2, 3, and 8-10 may be associated with apoptotic cell death. In fact, gene expression analysis revealed that the average cell viability was significantly associated with genes with a function in apoptotic cell death, especially pro-apoptotic FASTKD2, BNIP3L genes and anti-apoptotic TNFAIP8 and BCL2L2 genes. This correlation with both pro-apoptotic and anti-apoptotic genes suggests that there may be a complex live-death equilibrium in cultured HWJSCs kept in culture for multiple cell passages. In this study, the highest cell viability levels corresponded to the fifth and sixth HWJSC passages, suggesting that these passages should be preferentially employed in cell therapy or tissue engineering protocols using this cell type.

When loaded with the antiseptic CHX, this quaternary ammonium-based polymer coating released its contents in a controlled manner indicating its potential prophylactic use to reduce the risk of infection following PP mesh implantation.

IntroductionProsthetic mesh infection constitutes one of the major complications following hernia repair. Antimicrobial, non-antibiotic biomaterials have the potential to reduce bacterial adhesion to the mesh surface and adjacent tissues while avoiding the development of novel antibiotic resistance. This study assesses the efficacy of presoaking reticular polypropylene meshes in chlorhexidine or a chlorhexidine and allicin combination (a natural antibacterial agent) for preventing bacterial infection in a short-time hernia-repair rabbit model.MethodsPartial hernia defects (5 x 2 cm) were created on the lateral right side of the abdominal wall of New Zealand White rabbits (n = 21). The defects were inoculated with 0.5 mL of a 106 CFU/mL Staphylococcus aureus ATCC25923 strain and repaired with a DualMesh Plus antimicrobial mesh or a Surgipro mesh presoaked in either chlorhexidine (0.05%) or allicin-chlorhexidine (900 μg/mL-0.05%). Fourteen days post-implant, mesh contraction was measured and tissue specimens were harvested to evaluate bacterial adhesion to the implant surface (via sonication, S. aureus immunolabeling), host-tissue incorporation (via staining, scanning electron microscopy) and macrophage response (via RAM-11 immunolabeling).ResultsThe polypropylene mesh showed improved tissue integration relative to the DualMesh Plus. Both the DualMesh Plus and the chlorhexidine-soaked polypropylene meshes exhibited high bacterial clearance, with the latter material showing lower bacterial yields. The implants from the allicin-chlorhexidine group displayed a neoformed tissue containing differently sized abscesses and living bacteria, as well as a diminished macrophage response. The allicin-chlorhexidine coated implants exhibited the highest contraction.ConclusionsThe presoaking of reticular polypropylene materials with a low concentration of chlorhexidine provides the mesh with antibacterial activity without disrupting tissue integration. Due to the similarities found with the antimicrobial DualMesh Plus material, the chlorhexidine concentration tested could be utilized as a prophylactic treatment to resist infection by prosthetic mesh during hernia repair.

IntroductionPresoaking meshes for hernia repair with antiseptics prior to implantation could decrease the adhesion of microorganisms to the material surface and reduce the risk of antibiotic resistances. In this work, we evaluate chlorhexidine and allicin (natural antiseptic not yet tested for these purposes) against vancomycin as antiseptics to be used in the pretreatment of a heavyweight polypropylene mesh using an in vitro model of bacterial contamination.MethodsSolutions of saline, vancomycin (40 µg/mL), allicin (1,000 µg/mL), chlorhexidine (2%-0.05%) and the combination allicin-chlorhexidine (900 µg/mL-0.05%) were analyzed with agar diffusion tests in the presence of 106 CFU Staphylococcus aureus ATCC25923. Additionally, sterile fragments of Surgipro (1 cm2) were soaked with the solutions and cultured onto contaminated agar plates for 24/48/72 h. The antimicrobial material DualMesh Plus was utilized as positive control. At every time, the inhibition zones were measured and the bacterial adhesion to the mesh surface quantified (sonication, scanning electron microscopy). Cytotoxicity of the treatments was examined (alamarBlue) using rabbit skin fibroblasts.ResultsThe largest zones of inhibition were created by allicin-chlorhexidine. Chlorhexidine was more effective than vancomycin, and allicin lost its effectiveness after 24 h. No bacteria adhered to the surface of the DualMesh Plus or the meshes soaked with vancomycin, chlorhexidine and allicin-chlorhexidine. On the contrary, saline and allicin allowed adherence of high loads of bacteria. Vancomycin had no toxic effects on fibroblasts, while allicin and chlorhexidine exerted high toxicity. Cytotoxicity was significantly reduced with the allicin-chlorhexidine combination.ConclusionsThe use of antiseptics such as chlorhexidine, alone or combined with others like allicin, could represent an adequate prophylactic strategy to be used for hernia repair materials because soaking with these agents provides the mesh with similar antibacterial properties to those observed after soaking with vancomycin, similar to the effect of DualMesh Plus.