A novel immobilized Ca 0.6 Ho 0.4 MnO 3 photocatalyst has been developed with high photocatalytic activity for Rhodamine 6G (Rh6G) photodegradation under visible light irradiation. The nanocrystalline Ca 0.6 Ho 0.4 MnO 3 films were successfully deposited by RFmagnetron sputtering on unheated quartz glass substrates using Ca 0.6 Ho 0.4 MnO 3 powder as sputtering target and its photocatalytic functionalities have been explored. The visible-lightresponsive photocatalytic activity of Ca 0.6 Ho 0.4 MnO 3 films was evaluated by the photodegradation of Rh6G aqueous solutions under visible light irradiation. The reusability of Ca 0.6 Ho 0.4 MnO 3 films on fresh dye samples was studied, showing an efficient reuse, without decreasing the photocatalytic decolorization efficiency. Furthermore, X-ray diffraction of the reused films did not reveal additional phases indicating high photochemical stability of the films even after reusing them in successive runs. The photocatalytic efficiency of the nanocrystalline Ca 0.6 Ho 0.4 MnO 3 films was further compared with TiO 2 films also produced by sputtering and the results revealed a significant improvement in photocatalytic activity over TiO 2 under visible light irradiation. Almost complete photodecolorization of a 5 ppm Rh6G solution was achieved in 4 h, while only 64% of dye degradation was observed in TiO 2 photoassisted process. This work provides a feasible route to fabricate high-performance immobilized ABO 3 -based nanomaterials, and the finding opens up a new venue for designing visible light sensitive ternary compounds for photocatalytical applications.
With the aim of producing materials with enhanced optical and photocatalytic properties, titanate nanotubes (TNTs) modified by cobalt doping (Co-TNT) and by Na(+)→ Co ion-exchange (TNT/Co) were successfully prepared by a hydrothermal method. The influence of the doping level and of the cobalt position in the TNT crystalline structure was studied. Although no perceptible influence of the cobalt ion position on the morphology of the prepared titanate nanotubes was observed, the optical behaviour of the cobalt modified samples is clearly dependent on the cobalt ions either substituting the Ti(4+) ions in the TiO6 octahedra building blocks of the TNT structure (doped samples) or replacing the Na(+) ions between the TiO6 interlayers (ion-exchange samples). The catalytic ability of these materials on pollutant photodegradation was investigated. First, the evaluation of hydroxyl radical formation using the terephthalic acid as a probe was performed. Afterwards, phenol, naphthol yellow S and brilliant green were used as model pollutants. Anticipating real world situations, photocatalytic experiments were performed using solutions combining these pollutants. The results show that the Co modified TNT materials (Co-TNT and TNT/Co) are good catalysts, the photocatalytic performance being dependent on the Co/Ti ratio and on the structural metal location. The Co(1%)-TNT doped sample was the best photocatalyst for all the degradation processes studied.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.