We compared the surface free energies and dentin bond strengths of two-step self-etch systems with and without an oxygen-inhibited layer. The adhesives were applied to self-etching primer-treated dentin surfaces of bovine incisors, after which the teeth were light-irradiated and the oxygen-inhibited layer was left intact or removed with ethanol. We determined surface free energies (γ S ) and their components by measuring the contact angles of three test liquids placed on the cured adhesives. We also measured the dentin bond strengths of chemically cured resin composite to the adhesives, with and without the oxygen-inhibited layer. For all surfaces, the estimated surface tension component,
This study evaluated the influence of an oxygen-inhibited layer on the surface free energies of three single-step self-etch adhesives and on the bond strength of chemical-cured resin. Adhesives were applied to bovine dentin and light irradiated, and the oxygen-inhibited layer was either retained or removed. Surface free energies were determined by measuring the contact angles of test liquids placed on the cured adhesives. Dentin bond strengths of chemical-cured resin with and without the oxygen-inhibited layer were measured. Ultrastructural observation of the restorative-dentin interface was made by scanning electron microscopy. For all surfaces, values of the estimated surface tension component, Lifshitz-Van der Waals force (γS(LW)), were relatively constant. Values for the Lewis acid (γS(+)) component increased slightly when the oxygen-inhibited layer was removed, whereas those of the Lewis base (γS(-)) component decreased significantly. The bond strength of the chemical-cured resin composite was significantly higher in specimens without an oxygen-inhibited layer (7.6-8.0 MPa) than in those with an oxygen-inhibited layer (4.8-5.2 MPa). Small gaps between adhesive and resin composite were found for the group with an oxygen-inhibited layer. These results indicate that the absence of an oxygen-inhibited layer in single-step self-etch adhesives promotes higher dentin bond strength of the chemical-cured resin.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.